Single-atom catalytic growth of crystals using graphene as a case study

REVIEW ARTICLE OPEN Single-atom catalytic growth of crystals using graphene as a case study Xiaoqin Yang 1,2,3,10 , Yu Liu 1,10 , Huy Q. Ta 4 , Ehsan Rezvani 5 , Yue Zhang 4 , Mengqi Zeng 6 , Lei Fu 6 , Alicja Bachmatiuk 7 , Jinping Luo 2 , Lijun Liu 2 ✉and Mark H. Rümmeli 1,4,8,9 ✉ Anchored Single-atom catalysts have emerged as a cutting-edge research field holding tremendous appeal for applications in the fields of chemicals, energy and the environment. However, single-atom-catalysts for crystal growth is a nascent field. Of the few studies available, all of them are based on state-of-the-art in situ microscopy investigations and computational studies, and they all look at the growth of monolayer graphene from a single-atom catalyst. Despite the limited number of studies, they do, collectively, represent a new sub-field of single-atom catalysis, namely single-atom catalytic growth of crystalline solids. In this review, we examine them on substrate-supported and as freestanding graphene fabrication, as well as rolled-up graphene, viz., single-walled carbon nanotubes (SWCNT), grown from a single atom. We also briefly discuss the catalytic etching of graphene and SWCNT’s and conclude by outlining the future directions we envision this nascent field to take. npj 2D Materials and Applications (2021) 5:91 ; https://doi.org/10.1038/s41699-021-00267-4 INTRODUCTION Catalysts are a major contributor to the global economy. Over 90% of chemical processes require catalysts and there is a continuous demand for the development of more effective, inexpensive, and green catalysts to secure a sustainable future for our society 1 .As defined by Berzelius in 1835, a catalyst is a substance capable of accelerating the rate of a chemical reaction without being consumed 2 . Broadly speaking, there are two groups of catalysts, namely, homogeneous catalysis in which the catalyst is in the same phase as the reactants during the reaction, and heterogeneous catalysis where the catalyst and reactants are in two distinct phases. Because of challenges in separating homogenous catalysts from the reaction product as well as the fact that most are somewhat thermally unstable, most industrial catalysts (ca. 80%) are heterogeneous catalysts 1,3 . Typically, heterogenous catalytic properties are sensitive to their surface heterogeneity and structure. For instance, metal catalysts are affected by their terminating atom coordination and so steps sites, kinks, vacancies, staking faults and twin boundaries all affect their performance. Moreover, the size of metal particles is also an important factor governing performance 4 and has helped drive the use of nanoparticles as catalysts. However, because of surface defects it is near impossible to fabricate two identical nanoparticles. One approach to address this complex issue is to reduce the size of a metal particle down to the atomic level, viz., a single atom serving as a catalyst and in this case there is no longer any surface heterogeneity 1 . Aside from providing high specific activity, singleatom catalysts (SAC) reduce cost and this is particularly important for expensive noble metals such as Pt, Pd, Ru, Rh and Ir which are important to the petrochemical industry, medicine production, environmental protection and energy applications 5 . Single-atom catalysts are nearly always prepared on a support material (e.g. metal oxide, metal carbide, carbon nitride, graphene and various other two-dimensional (2D) materials) 6,7 and can even be produced at scale now 8 . SAC’s have compelling properties in that each atom is accessible for the catalytic reaction (100% atomic efficiency), often the metal atom-support interaction enhances charge transfer between the two and they have unsaturated coordination unlike metal clusters which can lower activation energies 7,9 . SACs resemble heterogenous catalysts since they are immobilized on supports that can be relatively easily separated and re-used. While they also resemble homogeneous catalysts since the strong metal atom-support interactions yield electronic properties similar to those in organo-metallic complexes 7 . SACs are advantageous in comparison to other heterogeneous catalysts because one can also tune the coordination environment of a single atom. Typically, this is achieved by altering the type of coordinating atoms on the support 6 . Indeed, the use of isolated single atoms is the most effective method with which to obtain optimal active sites in corresponding catalysts so as to maximize the metal atom efficiency and maintain the necessary catalytic performances 5,10,11 . The field of SACs is a highly dynamic and fast-evolving field and can be expected to continue to develop strongly. However, despite the growing body of research on SACs, very little research exists on the use of single atoms for the catalytic growth of crystalline materials.Remarkably, in our extensive literature survey we only found examples based on the growth of a single crystalline material - graphene. Perhaps this is not surprising given the large body of research on graphene and moreover, as a single element 2D material it is technically less challenging to investigate. Of the few studies we found, all are based on 1 Soochow Institute for Energy and Materials Innovations, College of Energy, Collaborative Innovation Center of Suzhou Nano Science and Technology, Key Laboratory of Advanced Carbon Materials and Wearable Energy Technologies of Jiangsu Province, Soochow University, Suzhou 215006, China. 2 School of Energy and Power Engineering, Xi’an Jiaotong University, No. 28, Xianning West Road, Xi’an, Shaanxi 710049, China. 3 Gusu Laboratory of Materials, No. 388, Ruoshui Road, Industrial Park, Suzhou 215123, China. 4 Leibniz Institute for Solid State and Materials Research Dresden, P.O. Box 270116, D-01171 Dresden, Germany. 5 School of Mechanical and Materials Engineering, University College Dublin, Dublin 4, Ireland. 6 College of Chemistry and Molecular Sciences, Wuhan University, Wuhan 430072, China. 7 Polish Center for Technology Development (PORT), Ul. Stabłowicka 147, Wrocław 54-066, Poland. 8 Centre of Polymer and Carbon Materials, Polish Academy of Sciences, M. Curie-Skłodowskiej 34, Zabrze 41-819, Poland. 9 Institute of Environmental Technology, VŠB -Technical University of Ostrava, 17 Listopadu 15, Ostrava 708 33, Czech Republic. 10 These authors contributed equally: Xiaoqin Yang, Yu Liu. ✉email: [email protected]u.cn; [email protected] www.nature.com/npj2dmaterials Published in partnership with FCT NOVA with the support of E-MRS 1234567890():,; state-of-the-art in situ microscopy investigations as well as supporting theoretical studies. Despite the limited number of studies for SAC crystal growth, they do, collectively, represent a new sub-field of SACs, namely single-atom catalytic growth of crystalline solids. The use of SACs for crystal growth is crucial at the nanoscale, because, as for bulk solids the material’s crystal structure determines its properties, however, at the nanoscale the location and position of each atom becomes critically important. Thus, to fabricate such structures usefully for application, both with known and novel and as yet to be discovered materials, a prerequisite is to synthesize these materials with atom precision. Top down structuring at these levels, while having been so successful (for example in the microelectronics industry) struggles evermore as a manufacturing process at the nanoscale these days as few atom or single atom precision becomes a precondition. Thus, the ability to develop bottom-up approaches, where material is added with atomic precision is crucial. In this context, it becomes self-evident that the ability to construct crystals using a single catalyst atom has advantages, because in affect an atom serves as a tool with which to add atoms and the tool is of the same scale as the bricks (atoms) being used to construct a material. Indeed, the need for precision manufacturing at the atomic scale is ever more pertinent as we discover and develop new nanomaterials such as clusters (quantum dots), nanowires with variable properties and, of course, the rapidly developing 2D materials. All of these hold great promise for a number of applications ranging from bio-medicine, energy and electronics 12–14 . The need for atom precise control for materials fabrication is epitomized by the need for atom precise structuring of 2D materials for device fabrication. For example, in a simple case, the edge termination of graphene influences its properties, such as its chemical properties (e.g. hydrogen evolution reaction) 15,16 , its magnetic properties 17 , its mechanical properties 18 and its electronic properties 19–22 . Similar dependencies are found for other 2D layered materials such as the transition metal dichalcogenides (TMDs) 23–25 , the few atoms-thick layers of transition metal carbides, nitrides, or carbonitrides, commonly referred to as MXENES 26–28 . Such atom precise edge termination control will be imperative if we are to develop electronic circuits based on these 2D materials. Thus, to fabricate such materials from a bottom-up approach using a catalyst it becomes challenging to form the structure using a catalyst particle since the size of the catalyst particle is significantly larger than that of the edge structure and as a result can’t yield atom precise clean edges 29 . Using a single atom overcomes this obstacle. This is illustrated in Fig. 1below using graphene as an example. The two canonical types of graphene edges are also provided, namely zigzag (ZZ) and arm-chair (AC) edge termination are firstly presented schematically (panel a). Then a schematic representation of a single atom growing a single-atom layer on graphene with only a single-atom layer growing is presented (panel b) and in panel c the rough edge termination typically observed from catalyst nanoparticles and clusters at graphene edges is presented. The use of single-atom catalysts for crystal growth with atomic precision is in its infancy and there remain many challenges. To highlight some of these challenges let us consider the case of a SAC for the growth of a device from a 2D material, e.g., graphene. To achieve growth one needs to first determine an appropriate catalyst atom and then nucleate a seed maintaining a SAC at an edge or place the catalyst atom at an edge of an initial seed. For Fig. 1 Schematic of edge growth from a single catalyst atom and from a catalyst nanoparticle. Panel ashows the zigzag and armchair edge termination of graphene. Panel bshows a single-atom edge layer being grown at a graphene edge from a single-atom catalyst and panel cshows the typically rough edge formed from a catalyst nanoparticle/cluster at a graphene edge (growth and etching). X. Yang et al. 2 npj 2D Materials and Applications (2021) 91 Published in partnership with FCT NOVA with the support of E-MRS 1234567890():,; atom precise growth, control of the edge atom will then be required, as well as systems to provide the appropriate feedstock etc. From these few aspects it is clear there are many hurdles ahead, but overcoming them presents enormous potential for atom scale crystal growth with many potential applications we have as yet to imagine or discover. At this early stage, we are only just beginning to show how single and even paired atoms can be used to grow 2D materials (namely graphene) and what factors can be used to control the SACs and even cause them to switch between catalytically growing or catalytically etching a material. The road ahead appears exciting. In this review, we examine the studies that employ a SAC for the edge growth of graphene on a substrate and as a freestanding structure as well as the case of rolled-up graphene, viz., singlewalled carbon nanotubes (SWCNT). We also briefly discuss the catalytic etching of graphene and carbon nanotubes and finally discuss the future directions we envision this nascent field to take. SINGLE-ATOM SP 2 CARBON CRYSTAL GROWTH The potential for a catalytic role from single metal atoms to grow sp 2 crystalline carbon was predicted theoretically for graphene 30 and for single-walled carbon nanotubes 31 . As mentioned in the introduction the potential and relevance of SACs for 2D crystal growth were laid out. In particular, if one considers the importance of edge terminations on the properties of 2D materials and even device systems relying on single and few atoms, such as singleatom transistors 32,33 , molecular electronics 34 and thereby quantum electronics and logic at the atomic scale 35 . If we consider the case of graphene, the fabrication of edge terminations with atomic control we could construct entire integrated electrical circuits. Equally if we are able to control single atoms to grow and control the chirality of single-walled carbon nanotubes we could also build entire integrated electronic circuits from carbon nanotubes (see Fig. 2). Such technological developments will be groundbreaking and highlight the importance of developing the use of SAC’s for crystal growth and in particular sp 2 carbon nanomaterials. However, it is only in the last few years that experimental evidence for the growth of graphene from a single metal atom has started to emerge. This is because both high spatial and temporal resolution are required to provide an understanding of the reaction pathways. Thus far, two microscopy techniques have demonstrated their potential to provide direct observational information at the atomic scale. They are the transmission electron microscope and scanning tunneling microscopes for freestanding graphene growth and supported graphene growth studies, respectively. Here, we begin with the case of supported growth. Graphene growth on a substrate Shu et al. 36 conducted a comprehensive study on the stability of several graphene edge configurations on Cu (111) and other metal surfaces during chemical vapor deposition (CVD) growth conditions using density functional theory (DFT) calculations. The work found that the termination of armchair (AC) edges by individual Cu atoms was energetically preferred as compared to zigzag (ZZ) edges that tend to keep their pristine structure. Moreover, the study showed that the Cu atom passivation of AC edge sites on the graphene significantly lowers the barrier of incorporating carbon atoms into the growing graphene edge from 2.5 to 0.8 eV. This results in very fast growth at the AC edge of the graphene. As a consequence, the authors state, that, on the basis of the classical theory of crystal growth, the ZZ edge should be the dominant edge of growing graphene edges in agreement with broad experimental observations 36 . In another work, the same group looked at the role of Ni adatoms at graphene edges (in comparison to Cu) using DFT calculations. The study showed that C species can be inserted (added) through individual Ni atoms at kink sites at the edges 37 . Indeed, mobile adatoms which are commonly present on metal surfaces at elevated temperatures are involved in several chemical processes taking place on surfaces and at the solid-liquid interface 38,39 . Fig. 2 Schematic of integrated electronic circuits from graphene ribbons and single-wall carbon nanotubes. a schematic and circuit from defined graphene ribbons (inspired by ref. 53 ). bSchematic showing controlled growth of a single-walled carbon nanotube from a SAC (left) leading integrated single-walled carbon nanotube circuit components (right). X. Yang et al. 3 Published in partnership with FCT NOVA with the support of E-MRS npj 2D Materials and Applications (2021) 91 In a detailed high-speed STM characterization study on epitaxial graphene growth on Ni (111) the researchers observed single Ni atoms at kink sites on the graphene edges at elevated temperatures 40 . The time resolution was on the order of milliseconds. The edge termination of the epitaxial graphene were identified as zigzag (zz) and Klien (k) edges. For both edges kink sites (where there are interruptions on the last two C rows) were observed with individual Ni atoms. These kink sites were shown to act as nucleation centers for graphene growth. Growth was shown to proceed from the kink site by the orderly completion of the two interrupted carbon rows while moving the kink ahead. The observational data pointed to mobile Ni adatoms diffusing along the edges and that these single Ni atoms at kink sites are directly involved with the growth process. This is in agreement with the above discussed theoretical study which is in agreement with the above mentioned DFT studies 37 . Moreover, the experimental team also conducted molecular dynamic (MD) studies. The MD studies at a temperature of 710 K showed Ni adatoms to move randomly over the bare metal surface until they reached a graphene edge. Once at a graphene edge the Ni atoms diffuse parallel to the edge and showed considerably longer residence times when encountering a kink site. Experimentally the STM image series showed that, in most cases, the adatoms presence was accompanies by C dimer attachment nearby strongly suggesting a catalytic role of the single Ni atom. Figure 3shows a sequence corresponding to the k edge. Two short-lived Ni adatom configurations can be identified at the kink sites (panels B, C, F, and G). Constant-height simulated images (panels D and H) matched the corresponding STM data. In short, the stable configurations observed by STM, as well as theory point to individual Ni atoms playing a catalytic role in the insertion of C at kink sites, viz. graphene growth while on a metal surface 40 . While synthetically grown graphene is mostly achieved on substrates, the above works show that the actual growth process is complicated and that there remains much to study, in particular regards growth on substrates involving a SAC. The only clear Fig. 3 Nickel adatoms at the graphene edges. A Ni adatom diffusing on a surface in a region delimited by graphene z (right) and k (left) edges with kinks. Two representative trajectories obtained by MD simulations with ReaxFF performed at 710 K for 100 ps are shown. Color palette for Ni trajectories: from green (initial position) to white (final position). The final steps are highlighted by increasing the ball size. B–I Short-lived configurations of Ni adatom at k-edge kinks: Band FHigh-speed STM images from movie S2 (20) (V=20 mV; I=7 nA). Cand G Laplace-filtered version of images from (B) and (F) with superimposed ball models. Dand Hconstant-height STM simulated images based on the calculated geometries (Eand I). Reproduced with permission from the American Association for the Advancement of Science 40 . X. Yang et al. 4 npj 2D Materials and Applications (2021) 91 Published in partnership with FCT NOVA with the support of E-MRS evidence thus far is for a Ni atom, but how other elemental SACs can be used, can SACs be used on differing substrates, what are the roles for differing environmental aspects (e.g., feedstock, presence of hydrogen, pressure etc), can multiple SACs be employed etc, are but a few of the critical questions that need to be explored when employing SACs for crystal grow on a substrate. One of the greatest challenges to explore SAC driven crystal growth, at least through direct observation studies, are the limited choices in characterization tools. STM has proven itself, but is still a challenging approach. We envision that in the future, electron transparent ultrathin substrates could be employed in dynamic in situ environmental TEM systems. TEM based studies may also pave the way for a broader set of synthesis conditions to be explored than that through STM based studies. Freestanding growth at graphene edges We now turn our attention to the case of single metal atoms at the edges of freestanding graphene. In all these experimental studies a TEM was used to study the individual metal atoms at the edge of the freestanding graphene. In some cases additional heating was provided to help drive the catalytic reaction, however, in most cases, electron irradiation is sufficient to drive the reaction. Details of the electron beam-specimen interactions that help drive the reaction can be found in reference 41 . The carbon feedstock for growth is obtained from hydrocarbon contamination within the TEM column 42 . We begin with the case of single iron atoms at graphene edges 43 . The iron atoms were provided from FeCl 3 which was used as an etchant during the transfer of the CVD grown graphene 44 . The Fe atoms attach to the edges more easily because of the larger binding energy of edges as compared to the basal plane of the graphene. The researchers 43 found two ubiquitous configurations of a single Fe atom residing at an AC edge. In the first configuration, an Fe atom incorporated into a five-atom ring forming a pentagon while in the second an Fe atom incorporated into a five-atom ring to form a distorted pentagon (i.e., substituting a C atom). However, when irradiated by the electron beam the Fe atoms diffuse along the graphene edge and at times incorporate additional carbon. Figure 4shows a cycle of the single Fe atom catalytically adding in two carbon atoms. In panels A–D a typical translocation of a single unit cell for an Fe at is shown. The Fe atoms changes from a pentagon structure and absorbs some carbon atoms. As it absorbs the carbon atoms it moves to the right (this is observed as a shadow line in panel C as the motion occurred during the image exposure). It then stops at a nearby location, again, forming a pentagon. Stick and ball models show the different atomic rearrangements of the process in panel E. While panel G shows the corresponding translocations added a micrograph of the process. During the process the single Fe atoms unit cell shifts to the right on a ZZ edge, the whole cycle represents a single catalytic growth cycle for graphene from a Fe atom incorporating two C atoms 43 . The external carbon atoms arise from hydrocarbon contamination with the TEM 42 . It is also worth noting that the in situ TEM studies on Fe atoms at graphene edges, the researchers also observed the catalytic etching of graphene, which, is discussed later. A similar study was conducted to investigate the behavior of Cr atoms at graphene edges 45 . Upon electron beam irradiation the Cr atoms diffuse along the edge and after their migrations, new carbon atoms were found to have been incorporated between the Cr atoms initial and final position. This led to the formation of new hexagonal structures leaving a ZZ edge. Figure 5shows an example of this process. The authors conducted a statistical analysis of the number of new hexagons forming at an open graphene edge and found one to six formed within a one-frame-per-second micrograph capture rate. Unlike the case for Fe atoms at graphene edges, with Cr atoms no etching of the graphene was observed. The Cr atom at graphene Fig. 4 One cycle of catalytic growth of graphene edge. A–DA series of high-resolution TEM images or 4 s; the Fe atom is highlighted as a red dot, whereas the nearby carbon atoms are highlighted as black dots. The dark shadow line, which is highlighted by the red circle in (C), is because of the motion of the Fe atom during exposure time. (Scale bar: 0.5 nm.) EThe corresponding atomic structures for (A–D). FThe combination of (A–D), which shows the trace of the Fe atom during the one-unit cell translocation. (Scale bar: 0.5 nm.) GThe atomic structure for the whole growth process (two carbon atoms are added). Reproduced with permission from National Academy of Sciences 43 . X. Yang et al. 5 Published in partnership with FCT NOVA with the support of E-MRS npj 2D Materials and Applications (2021) 91 edge study also included a MD study comparing Fe and Cr atoms at a graphene edge. The MD study showed confirmed both Fe and Cr single atoms can catalytically grow graphene; however, there were some differences. The Fe atom was shown to be far more dynamic both from a temporal and spatial perspective. These differences were attributed to their energetic and kinetic stability and these aspects affect the catalytic efficiency of the atoms in that an efficient SAC should have a good balance between stability and migration. Stability is important to provide a nucleation site, which is needed to attract C atoms for the catalytic process. However, the atoms potential to migrate is also important to keep the catalyst atom active along the graphene edge and avoid poisoning. The comparative MD study on Cr and Fe atoms at graphene edges indicated that Cr is a more efficient SAC as compared to Fe for graphene edge growth 45 . In another study, the role of single Cu atoms at graphene edges was investigated 46 . They observed Cu atoms frequently in pentagon structures at the graphene edge (similar to the case for Fe described above). With electron irradiation and heating (150 o C or 300 o C) they observed graphene growth mediated by a single Cu atom. Figure 6shows examples of the growth. Panels A and B show before and after examples of the growth. The shaded region in panel B shows extensive growth after 3 min of irradiation. Panels C to G show more details of the actual growth process. In a previous study by the team, they showed substitutional Cu atoms can promote the rotation of C–C bonds in graphene 47 . Such C–C rotations can convert pentagonheptagon pairs into hexagons which is what they observed in the Cu atoms at graphene edge study (panels C and D) which triggered further rotations as shown in panel E. Panels F and G provide another example of a Cu atom translocation over a different edge system and the incorporation of new C atoms as it does so, further confirming the catalytic growth of graphene by a single Cu atom. A more recent study examined the role of Sn atoms at graphene edges 48 . The study examined single Sn atoms (monomers) as well as Sn atom pairs (dimers) as SACs. Both graphene growth and etching was observed from both monomer and dimer SACs, and the switching mechanism between growth or etching is discussed a little later. The experimental data and supporting DFT studies showed a good correlation between the observed frequency of Sn-graphene bonding configurations and their relative energies (i.e., energy difference relative to the most commonly observed configuration of an Sn atom residing at an armchair position at the graphene edge). In terms of the dynamic diffusion of Sn atom SAC pairs a remarkable tendency was observed, namely, a synchronized diffusion between the two atoms (for growth and etching) was observed (see Fig. 7). More in-depth experimental and theoretical investigations revealed the synchronized diffusion occurred in a step-wise shuffle of the two atoms, viz. after the first Sn SAC atom shifts, the second one follows, rather than a hopping process which was also postulated as a possible mechanism. While most observations showed Sn dimer SAC diffusion to occur synchronously, occasionally the Sn pair would diffuse in opposite directions and the dimer would collapse to two Sn monomers. A detailed statistical analysis of the dimers diffusion showed the vast majority diffused as a dimer (indicating an attractive interaction which was also supported by DFT studies). Moreover, the study showed an edge dependency, such that ZZ edges tended to lead to dimer collapse, while AC edges and chiral edges tented to favor dimer synchronized diffusion. Calculations of the relative binding energies showed two interesting aspects (see Fig. 8). In the first, the relative binding energy for zigzag edges is positive and indicates that ZZ edges favor individual Sn SACs rather than dimer SACSs. Thus, paired SACs (dimers) are likely to separate (collapse) on diffusing, exactly as was observed experimentally. Secondly, in the case of Sn single and binary atoms at AC edges, the binding energy for Sn pairs (dimers) was found to be significantly lower than for a single Sn atom. Thus, the study explains why when the binary SAcs are at AC sites they prefer to synchronize their diffusion such that as soon as one atom moves, the second will follow in the same direction (shuffle) so as to minimize their energy and it explains why, experimentally, the synchronized diffusion of binary atoms was observed so often and moreover, why this was found predominantly at armchair sites 48 . Another important SAC is Ni which is a well-known and commonly used transition metal catalyst material in its bulk form due to its availability and cost. To this end, we have been investigating Ni atoms as SAC candidates for graphene growth. Initial studies show that Ni SACs can effectively grow graphene in situ in TEM under electron beam irradiation. At times we observe Ni SACs to catalytically etch graphene (data not shown). An example of a Ni SAC catalytically growing graphene is presented in Fig. 9. Figure 9(a) shows a Ni atom initially residing in a hexagonal location at a graphene edge (i.e., the Ni atom substitutes a C atom). After 20.25 sec. the Ni atom shifts to the left and locates in an armchair configuration (pentagon). Its former location now has Fig. 5 Catalytic growth of graphene by a single Cr atom at the graphene edge under electron beam irradiation. A–C, with partial stickand-ball models to aid viewing (D)–(F), image simulations of the growth process G–I, and complete stick-and-ball models J–L. The blue ball indicates Cr, whereas red balls and green arrows signify new C atoms. All scale bars are 1 nm. Reproduced with permission from Springer 20 . X. Yang et al. 6 npj 2D Materials and Applications (2021) 91 Published in partnership with FCT NOVA with the support of E-MRS a C atom, indication growth. Where this C atom came from is unclear. It could have come from the position the Ni atom translocated to, or from the Klein edge that existed at the far left of the initial system (panel a), or from the vacuum. Regardless, the translocation confirms the catalytic action of the Ni atom at a graphene edge. To summarize this section a number of metal atoms (Fe, Cr, Cu, Sn, and Ni) all show the potential as SACs for crystal growth, at least for graphene. Moreover, in all instances a single or few carbon atoms get incorporated during the catalytic growth cycle of the metal SACs, confirming that in reality SACs offer the potential to grow graphene edges with atom precision. Equally attractive is the potential for single atoms to grow single-walled carbon nanotubes with atomic precision (and hence chiral control). Reportedly, the Nobel Laurette Richard E. Smalley, proposed a single catalyst atom could grow a single carbon nanotube by adding C at an open edge (see the bottom left panel in Fig. 4). In the next section, we examine SAC growth of singlewalled carbon nanotubes (SWCNT). SWCNT Growth at Edges Single-walled carbon nanotubes are, in essence, rolled-up tubules of graphene strips. Depending on the manner in which the graphene strip is rolled (their so called chirality), the tubes electronic properties can be either semiconducting or conducting. Moreover, SWCNT combining different chirality’s leads to interesting properties such that carbon nanotubes can serve as (ballistic) interconnects and devices (e.g., rectifiers, transistors etc.) 49 . Their controlled combinations can yield integrated electronic circuits. However, at this stage, such integrated circuits remain challenging to produce since it requires fabrication control at the atomic scale. SACs could potentially provide a means to overcome this hurdle. While we did not find any examples of a SACs growing a singlewalled carbon nanotube experimentally, we did find a theoretical study looking at a single Ni atom growing a freestanding SWCNT. The study was based on density functional total energy calculations. A temperature of 1200 o C was used. Figure 10 shows the intermediate steps involved in the catalytic growth of a SWCNT, as well as the binding energies. The study looked at the energetics and in the first scenario a Ni atom forms a pentagon structure (panel A1), then a carbon atom gains energy (4.5 eV) by forming a pentagon defect (panel A2). The high mobility Ni atom nearby reacts with the carbon to form a hexagon (panel A3) The authors argue that an incoming C atom would then push out the substitutional Ni atom (panel A4). Then, because of the weak attachment energy (inferred from the geometries in panels A4 and A5), the Ni atom can continue its diffusion along the edge and further grow the SWCNT. Further intermediate steps for carbon insertion are provided in panels A1’to A5’for a different catalytic cycle. Both catalytic cycles are exothermic and occur with no activation barriers which would suggest a high reaction rate. In short, using concerted exchange mechanisms, the single Ni atom at the open SWCNT edge can catalyze growth by the continued formation of hexagons. As an early step to investigate the propensity if Ni SAC’sto catalytically grow sp 2 carbon we explored their SAC behavior in situ in a TEM at graphene edges under electron irradiation. As discussed at the end of the previous section, indeed, Ni SACs can grow graphene. The presented example (Fig. 9does not, however, show growth from AC sites as theoretically predicted 31 , although we do observe Ni atoms at AC edges (see Fig. 11) and so we may yet observe the predicted growth. Moreover, the synthesis conditions in our studies are rather different in that the reaction is driven by an electron beam and is conducted at room temperature. We also plan on conducting experimental studies with SACs at the end of open SWCNT. There is much to be explored regards SACs and SWCNT growth. Fig. 6 Cu atom behavior at graphene edges. A TEM image of two Cu atoms at the graphene edge. BTEM image taken ∼3 min after (A). C–GTEM images and schematic atomic models showing the Cumediated mending of the graphene edge. All of these TEM images were extracted from Movie S1 in the online supplementary data at http://stacks.iop.org/APEX/10/025104/mmedia, where (A) corresponds to t=0 s. Scale bars represent 0.5 nm. Reproduced with permission from the Japan Society of Applied Physics 46 . X. Yang et al. 7 Published in partnership with FCT NOVA with the support of E-MRS npj 2D Materials and Applications (2021) 91 SINGLE-ATOM SP 2 CARBON CRYSTAL ETCHING While the focus of this article is on the growth of graphene from SACs, it is worth briefly looking at SACs potential to etch graphene catalytically. We begin with the case of Fe SACs which although they can grow graphene under electron beam irradiation, as discussed above, they can also etch graphene 17 . In that study, the conditions to determine which catalytic process occurred was not clear since the conditions were more or less the same. Another example is that of Cr, which on one study was only found to grow graphene and no etching was observed 20 . While in another study Fig. 7 Activity of an Sn dimer along a graphene edge under electron irradiation. a–cHRTEM images showing binary atoms activity. d–f HRTEM images with partial ball models to aid viewing. g–iHRTEM images showing possible atom hopping activity. j–lHRTEM images showing possible atom shuffle activity. The rose-red balls indicate the Sn atom, and the translucent rose-red balls represent the previous positions of the Sn atom. Dose ca. 1.8 × 10 6 A/m 2 , and all scale bars are 0.5 nm. Reproduced with permission from Wiley-VCH GmbH 48 . Fig. 8 Analysis of diffusion and relative binding energies for Sn monomers and Sn dimers at different graphene edges. a The relative occurrence diffusion behavior (as a pair or splitting) for different Sn dimer/edge configurations under electron irradiation. bThe optimized configurations of Sn monomers and dimers at a zigzag edge. cThe optimized configurations of Sn monomers and dimers at an armchair edge. Reproduced with permission from Wiley-VCH GmbH 48 . X. Yang et al. 8 npj 2D Materials and Applications (2021) 91 Published in partnership with FCT NOVA with the support of E-MRS looking at Cr, Ti, Pd, Ni, Al and Au, the authors claim to have only observed etching from these SACs 50 . This might be due to differences in the electron beam conditions, given that in the study with Cr SACs where only growth was observed, the imaging mode was in TEM (parallel imaging) while in the latter study the scanning TEM (STEM) mode was used. Moreover the latter article did not present analytical data confirming the presence of Cr atoms at the graphene edge. In another TEM study, the use of Pt SACs at graphene edges at the elevated temperatures of 150 o Cor 300 o C were investigated and only etching was observed. In the same study, Au atoms at graphene edges observed in TEM at room temperature showed neither catalytic etching or growth 51 . Thus, the contradictory results between the different studies highlight a need for careful studies on the actual conditions implemented. In terms of SAC for graphene etching, Si, a nonmetal atom, has also been shown to catalytically etch graphene 24 . In this study, the researchers were able to form clean graphene edges or pores from Si SACs under electron beam irradiation (see Fig. 12). A recent study exploring single-atom and binary Sn SACs, an interesting concept, based on Au nanoparticle catalyst action, was postulated to explain the observation that in some cases SAC’s catalytic behavior followed either growth or etching despite similar or identical in situ TEM conditions 48 . To explain this fact they argue, the atoms follow exactly the same catalytic action when growing or etching a graphene edge. The difference lies in where the SAC obtains a carbon atom from and where it then deposits that captured carbon atom during the dynamic catalytic action. This is illustrated in Fig. 13, panel a. During the first catalytic step on the left, a C atom from the vacuum is captured by the Sn catalyst atom and then deposited at the graphene edge and this step represents growth. While on the right example a C atom from the graphene edge is captured by the Sn SAC and then the C is ejected to the vacuum and this cycle represents etching. However, to the Sn SAC there is no difference in its catalytic action since it simply captures a C atoms and then releases/deposits it somewhere else. However, the more costly cycle energetically will be the capture of a C atom from a graphene edge, as compared to C from the vacuum, since additional energy tip extract the C from the graphene edge is required. Thus in this argument, by controlling the supply of C atoms one can control if a SAC grows or etches Graphene. The catalytic process of an Sn SAC in the presence of a C supply in the vacuum (for graphene growth) is Fig. 9 Catalytic growth (C incorporation) at a graphene edge by a diffusing Ni SAC. a–bHRTEM images showing the Ni atom before and after catalytic activity. c–dHRTEM images with added balls to aid viewing. Ni is rose colored and the added C atom is in red. e–fImage simulations of the HRTEM images. g–hComplete stick-and-ball models of the structures used for the image simulations. Note: The red line is the reference line. All scale bars are 5 Å. Fig. 10 The intermediate steps involved in the catalytic growth of a SWCNT as well as the binding energies. A Schematic diagram of intermediate steps involved in the catalytic annealing of pentagon defects at the growing nanotube edge by a concerted exchange mechanism, leading to defect-free growth. BCorresponding binding energies of the two carbon atoms and one Ni atom to the nanotube. Reproduced with permission from the American Physical Society 31 . X. Yang et al. 9 Published in partnership with FCT NOVA with the support of E-MRS npj 2D Materials and Applications (2021) 91