Arsenic Removal in Aqueous System to Synthesized, Characterized Thiol and Sulfonium Integrated Starch Biopolymer: An Innovative Approach

1 Available online at www.derpharmachemica.com ISSN 0975-413X CODEN (USA): PCHHAX Der Pharma Chemica, 2023, 15(5): 1-13 (http://www.derpharmachemica.com/archive.html) Arsenic Removal in Aqueous System to Synthesized, Characterized Thiol and Sulfonium Integrated Starch Biopolymer: An Innovative Approach Vishal Priya* Department of Chemistry and Biochemistry, CSK Himachal Pradesh Krishi Vishvavidyalaya, Himachal Pradesh, India *Corresponding author: Vishal Priya, Department of Chemistry and Biochemistry, CSK Himachal Pradesh Krishi Vishvavidyalaya, Himachal Pradesh, India, E-mail: [email protected] Received: 17-October-2019, Manuscript no: DPC-23-103883, Editor assigned: 22-October-2019, PreQC No: DPC-23-103883 (PQ), Reviewed: 05-November-2019, QC No: DPC-23-103883, Revised: 30-June-2023, Manuscript No: DPC-23-103883 (R), Published: 28-July-2023, DOI: 10.4172/0975-413X.15.5.1-13 ABSTRACT The contamination of arsenic groundwater is the most serious global concern and responsibility for the death rate per year. Complete removal of arsenic through the conventional method is very difficult and cost consuming. We have synthesized the starch thiomer, sulfonium starch and iron immobilized starch derivatives for the removal of As (III) and As (V) from the aqueous system. The batch experiments were performed as a function of initial As (III) and As (V) concentrations, contact time and pH values. The results supported a little preferential sorption for As (V) (95%) in comparison to As (III) (92%) via thiomer, while sulfonium structure showed similar affinity for As (III) and As (V) sorption (92.7% for As (III) and 93% for As (V)) at pH 5.0. The present study also supported that synthesized thiomer and sulfonium structure are selective to arsenic and only marginal effect has been observed with competitive anions except for phosphate. The SEM-EDX studies confirmed the arsenic sorption mechanism of synthesized starch derivatives. Isotherm studies indicated that the Langmuir model is preferential, while in kinetics pseudo-second-order kinetic model is superior in describing the adsorption process for As (III) and As (V) adsorption through synthesized starch derivatives. The results of arsenic equilibrium adsorption at 35°C showed the endothermic nature of As (III) adsorption indicated by the positive ΔH° value support the result that As (III) adsorption decreased with temperature. The temperature effect on the intrinsic kinetics of As (V) adsorption for the present adsorbent is likely to surpass the endothermic effect on the adsorption reaction. Therefore, it is recommended that the excellent adsorption for As (III) and As (V) by thiomer and sulfonium structure would be a better solution and can be explored for commercialization in arsenic contaminated water for arsenic removal. Keywords: Water contamination; Arsenic; Starch; Immobilization; Adsorption; Biopolymer INTRODUCTION Arsenic is present ubiquitously in the earth’s crust and is a very noxious element even at very low concentrations. Arsenic exists in two predominate speciation As (III) and As (V), but the As (III) is more toxic than As (V). As (III) is a neutral species and is very difficult to remove from the aqueous system. Arsenic rarely exists in the free form of mostly occurs as sulfide or oxide ores and introduced in surface water and groundwater as a result of several natural and anthropogenic sources. Arsenic poisoning through contaminated drinking water causes the number of adverse effects on human health [1]. The global scenario is highlighted in Mexico, arsenic is present within the volcanic belt where arsenic-rich soils contaminate the groundwater. In Chile, arsenic is present in all ecosystems in the north of the country because of the predominance of quaternary volcanism in the zone. Between 1955 and 1970 in Antofagasta, the average arsenic level in the water was 0.598 mg/l. In India, most of the rural populations are exposed to arsenic by arsenic contaminated groundwater which is used for drinking purposes. World Health Organization (WHO) has recommended 10 ppb as the permitted level for arsenic. But the arsenic concentration has been exceeded to 10 ppb in Australia, China, USA, Bangladesh and India [2]. Several methods have been established for removal of arsenic from the aqueous system and among these adsorption is one of the best method for arsenic removal from aqueous system. This method stands due to a safe and easy process with high efficiency and regeneration capacity, least sludge making and low cost. Therefore, a number of adsorbents have been used for arsenic removal. The conventional adsorbents have some drawbacks like incomplete metal removal, high resources and operational cost, disposal of the residual metal sludge and less competence for smallscale industries. To overcome these problems, the development of effective and sustainable sorbent for complete removal of arsenic in both of the speciation from the water is a research priority [3,4]. Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 2 In recent years, the development of biopolymer based adsorbent for arsenic removal is attaining interest in research and -SH based materials are used as the most effective sorbent for heavy metal ions. Additionally, the iron based material shows a high affinity towards arsenic. Therefore, the immobilization of iron would be proved helpful to modulate the surface charge and to improve the extraction capability for arsenic [4]. Isotherms such as Langmuir, Freundlich models and kinetic models like pseudo-first-order, pseudo-second-order have been performed. Besides, the interference of different anions on adsorption of As (V) and As (III) has also been examined. Because of the above facts, the present effort is directed to synthesize green thiomers, sulfides and sulfonium adsorbents to remove arsenic in both of the speciation i.e. As (III) and As (V) from aqueous solutions. Sulfur fictionalization is targeted as the arsenic has a strong affinity for sulfur. To the best of our knowledge, there is no report to explore the possibility of sulfonium structure as an effective sorbent for arsenic removal. However, some reports for arsenic removal via anion exchanger have been reported, but they are only effective for As (V). The extensive experimental work has been carried out to estimate the performance of starch based sulfur derivatives for removal of As (III) and As (V). Therefore, a prospective benefit of this study is to characterize a new low-cost sorbent for the complete removal of As (V) and As (III) from aqueous solution (Figure 1) [5,6]. Figure 1: Sorption characterization of thiomer. MATERIALS AND METHODS Starch, thiourea, sodium arsenite and sodium arsenate were purchased from Hi-media and used as received. All other chemicals used were of analytical grade. The stock solutions of As (III) and As (V) were prepared by dissolving a known amount in double-distilled water. All glassware was cleaned with aqua-regia and rinsed with double-distilled water before use [7]. Preparation of starch derivatives Thiomer, sulfide and sulfonium functionalized starch were processed as per earlier reported procedure. In brief, initially the starch was functionalized with chloroacetylation and then the chloroacetylated starch was further modified to obtain the thiolated and sulfide starch. After that thiolated starch was functionalized by exhaustive alkylation in sulfonium structure. The synthesized products were extensively characterized for the reproducibility of results. Henceforth the synthesized products are referred to abbreviations i.e. thiomerm, sulfoniumm, sulfidem, sulfidec and sulfoniumc. In the nomenclature of products, m stands for microwave and c for the conventional method [8]. Preparation of iron coated starch derivatives Iron immobilized starch derivatives were prepared by placing 0.1 g of starch derivative in 0.01M FeCl3 solution and the solution was kept overnight. After that, the iron coated starch derivatives were collected and washed with distilled water. The product obtained was air dried for 24 h at 25°C and used for further experiments [9]. Characterization and instruments FTIR spectrums were recorded on Perkin-Elmer 4100. SEM (Jeol JSM 6100), Energy-dispersive X-ray analysis (EDX) of the synthesized products were recorded by Joel JSM 6100 instrument and UV-spectrophotometer systronics. The pH of solutions was adjusted with 0.1M HCl and 0.1M NaOH solutions and were monitored by using a pH meter [10]. Batch adsorption experiment Batch sorption experiments were performed with 0.1 g of synthesized sulfur derivative in 20 mL As (III) and As (V) solution at room temperature till equilibrium. The solution pH was adjusted for each experiment using 0.1M NaOH and 0.1M HCl. The residual concentration was determined from the test sets by removing 1.0 mL of aliquots at different contact times (i.e. 30 min, 1 h, 3 h, 6 h, 12 h and 24 h). The effect of various parameters such as pH (4.0 to 9.0) initial arsenic concentration (1.0 ppm, 6.0 ppm, 18 ppm, 30 ppm and 60 ppm) and presence of competitive ions (sulfate, nitrate, chloride and phosphate at 100 ppm) was investigated with contact time. All the experiments were performed in triplicate average of three observations was reported. The colorimetric technique has been carried out to quantify the As (III) and As (V) removal capacity of the synthesized starch derivatives at 220 nm and compare with a standard curve of unknown concentrations from the test-sets. The residual solids in test-sets were washed with deionized water and dried at 50°C. The dried sample was characterized for sorption by SEM-EDX. The adsorption isotherms were calculated by plotting the equilibrium adsorption capacity (qe) versus the equilibrium concentration of residual As (III) and As (V) Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 3 in the solution (Ce). The qe was calculated by the following formula [11]. Where qe is the equilibrium adsorption capacity (mg g-1), C0 and Ce are the initial and equilibrium concentration (ppm) of As (III) and As (V) respectively, V is the volume of aqueous phase (L) and m is the weight of polymer (g). The % uptake was calculated by the following relationship [12]. RESULTS AND DISCUSSION Successfully synthesized and characterized starch-based derivatives as per our earlier reported method. The detailed structure for the derivatives is depicted in Figure 1. The FTIR spectrum of thiomerm, sulfoniumm and iron immobilized adsorbent showed (4000 cm-1-500 cm-1). The characteristic peak due to S-H stretching vibration at 2841 cm-1 which indicates the modification of starch to the thiol structure. Peak at 1380 cm-1 confirms the presence of an ethyl group and hence displays successful derivatization to sulfonium ion structure (Figure 2). Figure 2: Structural unit for synthesized products. The adsorption peaks at 755 cm-1 and 762 cm-1 assigned to the Fe-OH stretching vibrations, which revealed the incorporation of iron in thiomer and sulfonium structure (Figure 3). Figure 3: FTIR spectra of (a) Starch thiomer and (b) Sulfonium starch. Effect of structure and concentration The synthesized starch derivatives were evaluated for effective removal of As (III) and As (V) removal from aqueous solution at 30 ppm and found that maximum percent uptake was 92%, 92.7%, 57% for As (III) and 95%, 93%, 37% for As (V) in thiomerm, sulfoniumm and sulfidem adsorbents after 24 h at 30 ppm. Conversely sulfoniumc and sulfidec adsorbents (prepared via conventional method) confirm low uptake i.e. 45% and 48% for As (III) and 55% and 34% for As (V) (Table 1). Thus it is concluded that starch derivatives i.e. thiomerm and sulfoniumm are preferential for sorption application in comparison to conventional products [13]. Therefore the further sorption studies for As (III) and As (V) were performed with these derivatives and hereafter they are named as thiomer and sulfonium starch. The results obtained with initial concentration varied from 1.0 ppm to 60 ppm, which depicts the effect of initial feed concentration of arsenic species on the removal capacity of thiomer and sulfonium with time (Figure 4 and Table 1). Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 4 Figure 4: FTIR spectra of iron immobilized (a) thiomer and (b) sulfonium starch. Table 1: Comparison of percentage uptake with structural effect. Polymer Percentage uptake Polymer Percentage uptake As (III) As (V) As (III) As (V) Thiomerm 92 95 Thiomerc - - Sulfoniumm 92.7 93 Sulfoniumc 45 55 Sulfidem 57 37 Sulfidec 48 34 Note: m=microwave; c=conventional In general, the arsenic removal efficiency increases with an increase in the initial arsenic concentration and equilibrium is attained within 6 hrs [14]. In iron immobilized adsorbent the percentage uptake is increased by the magnitude of ~5%. The percentage uptake of As (III) and As (V) with iron immobilized thiol starch is 97.6% and 98.4% respectively (Figure 5). Similarly, in iron immobilized sulfonium starch the percentage uptake is 96.8% and 97.7% respectively for As (III) and As (V). The marginal efficiency for arsenic removal in ionic state As (V) from aqueous solutions could be ascribed to the successful iron immobilization throughout the starch backbone (Figure 5). Figure 5: Schematic for iron immobilized of starch thiomer. Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 5 Arsenic speciation and surface charge of the thiolated and sulfonium starch The arsenic speciation is dependent on the pH and redox potential of the natural environment of the forms of water. Hence, pH value of water could significantly influence the adsorption performance of arsenic. Therefore, the effect of initial pH of arsenic solutions on the adsorption capabilities of thiomer was investigated for % removal of As (III) and As (V) by varying pH from 4.0 to 9.0 with (0.1 M HCl and 0.1 M NaOH) with 30 ppm concentration which was optimized concentration. The pH of the solution has significance and a restrictive outcome in the adsorption thiomerm and sulfoniumm adsorbents. It is perceptible that the As (III) and As (V) sorption capacity increases as the pH increases from 4.0 to 5.0, and then the sorption capacity decreases in alkaline medium from 6.0 to 9.0 pH. In the present study, As (III) and As (V) removal was observed maximum at 5.0 pH. The percentage removal of As (III) and As (V) by thiomer adsorbent was found 94% and 97% at 5.0 pH which is the maximum percentage uptake through all over the pH values. In the case of sulphonium adsorbent, the uptake revealed the lowest removal viz. 93% and 92%. Conversely, the conventional heating sulfidec sample had less uptake i.e. 57% and 37% for As (III) and As (V) respectively as compared to 48% and 31% in the case of sulfoniumc [15]. The decrease in sorption was evaluated at 6.0, 7.0, 8.0 and 9.0 pH with less percentage uptake. At acidic pH, the results are comparable and can be accounted for by a highly protonated adsorbent surface, which is capable of attracting arsenic species by electrostatic forces. Conversely, in higher pH values, the solution donates more hydroxide (OH-) groups and the presence of a large amount of OH-ions in the aqueous solution starts competing with arsenic for binding with the thiomerm and quaternary sulfoniumm groups. Similar results were also reported by the maximum removal rate for these adsorbents with positive surface charges at the 5.0 pH range and thereafter a decrease in the arsenic adsorption rates during increased pH values for biopolymeric quaternary and thiomerm products [16]. Thus, maximum sorption capacity on As (III) and As (V) by thiomerm and sulphoniumm adsorbents has been observed through microwave heating method at 5.0 pH which indicates performances of adsorbent was effective. However, at acidic pH starch thiomer and sulfonium are positively charged and leads to interaction with As (III) and As (V). Marginally favored domino effect of sorption for As (V) in acidic pH in comparison to As (III) can be explained by the strong electrostatic interaction between the protonated starch thiomer and anionic H2AsO4-, which is predominant species in this pH range. This also confirms the electrostatic nature of the arsenic sorption. Therefore, pH 5.0 was selected as optimum for solidphase extraction of arsenic for subsequent experiments. Comparison of arsenic adsorption by that the adsorption capacity of iron oxide decreases with an increase in pH. An increase in pH causes the decrease of surface positive charge, which results in a decreased attraction between thiomerm and sulphonium surfaces and arsenite and arsenate species. The difference in percentage uptake as a function of solution pH could be explained by the change of arsenic speciation and surface charge of the thiolated starch and sulfonium starch [17]. Redox potential (Eh) and pH are the most important factors to control the speciation of arsenic. Therefore, pH 5.0 was selected as optimum for solid-phase extraction of arsenic form subsequent experiments (Figure 6). Figure 6: Effect of time on percent uptake of (a) As (III) via thiomer (b) As (V) via thiomer (c) As (III) via sulfonium starch and (d) As (V) via sulfonium starch. Effect of competitive anions on As (III) and As (V) removal efficiency As well-known that various cations and anions may coexist with arsenic ions in natural waters. The interference of various coexisting ions such as Cl-, PO42-, SO42and NO3could influence aqueous phase equilibrium during As (III) and As (V) sorption. Subsequently, it is a necessity to test the adsorbent capability in such an environment. Cl-, SO42and NO3show negligible influence (2% to 8%) on As (III) and As (V) removal efficiency (Figure 7). The presence of PO42depicts comparatively highest decrease in As (III) and As (V) removal. In the presence of PO42the maximum removal efficiency decreases from 92% to 62% for As (III) and 95% to 60% for As (V) in thiomers. While in sulfoniumm the results support decreases from 92.7% to 58% for As (III) and 93% to 60% for As (V). The iron immobilized thiomer and iron immobilized sulfoniumm starch also follow the same trend and depict only negligible effect with Cl-, SO42and NO3on removal efficiency of arsenic (2% to 10%) (Figure 8). Similarly, in the presence of PO42the percent uptake decreases from 97% to 55% for As (III) and 98% to 58% for As (V) [18]. In the case of iron immobilized sulfoniumm starch the percentage uptake decrease from 96.8% to 60% for As (III) and 97.7% to 62% for As (V). The presence of co-existing ions affects the arsenic removal efficiency by thiomer and sulfonium adsorbent in the order of PO43->NO32->Cl->SO42-. The decrease in the adsorption efficiency is inferred due to competition for the binding sites of the adsorbent between phosphate and arsenic as phosphate and arsenic both have similar molecular structures (Figures 7 and 8). Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 6 Figure 7: Percent uptake of arsenic with (a) iron immobilized thiomer and (b) iron immobilized sulfonium starch. Figure 8: Effect of pH on arsenic sorption in (a) thiolated starch and (b) sulfonium starch. Adsorption isotherms Adsorption isotherms are used to ascertain the mechanism and distribution of the adsorbate between liquid and solid adsorbent phase at equilibrium during the process of removal. The experimental data of As (III) and As (V) removal by starch derivatives for different initial concentrations were plotted in linearized forms of Langmuir and Freundlich model [19]. Langmuir model is valid for monolayer adsorption over a homogenous surface with a finite number of active sites and identical adsorption energy. The linear equation that describes the Langmuir model is given as: Where qe is the amount of adsorbed arsenic per gram of sorbent (mg/g); Ce is the equilibrium concentration of adsorbate in the solution (mg/L); qm is the maximum adsorption capacity at monolayer coverage in mg/g; KL is the Langmuir equilibrium constant (L/mg). For further analysis of the adsorption process, a dimensionless constant separation factor RL is also calculated which reflects the essential characteristics of Langmuir adsorption. Where KL is the Langmuir constant and Co is initial arsenic concentration. The RL value has importance when it is between 0 and 1, where it indicates an effective interaction between the adsorbent and the adsorbate. Values greater than one indicates an unfavorable isotherm and RL equal to zero is accounted for an irreversible isotherm [20]. The Freundlich model is widely used to describe the adsorption of an analyte on a heterogeneous surface and is applies to monolayer chemisorptions and multilayer adsorption physisorption. The Freundlich isotherm is described as. Where qe is the amount adsorbed per unit mass of adsorbent (mg/g), Ce is the equilibrium adsorbate concentration in solution; Kf and n are the Freundlich constants related to the adsorption capacity and adsorption intensity respectively. Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 7 The adsorption isotherms were regressively simulated with the Langmuir and Freundlich models. The values of the relative parameters calculated from the two isotherm models (Tables 2 and 3). The R2 values of the Langmuir model are higher than those of the Freundlich model, indicating that the Langmuir model fits the adsorption isotherms better than the Freundlich model. This suggests that the adsorption of As (III) and As (V) on thiolated starch and sulfonium starch is monolayer adsorption. The RL values are also calculated between 0 and 1 which indicates favorable adsorption. Both the models are then compared for experimental and theoretical adsorption capacity. It is indicated, that the Langmuir model confirms a slightly preferential match with the value of sorption capacities obtained from the experimental (Figure 9). Figure 9: Effect of competitive ions on percent uptake of (a) As (III) via thiomer (b) As (V) via thiomer (c) As (III) via sulfonium starch and (d) As (V) via sulfonium starch. Table 2: Langmuir adsorption isotherm parameters. Langmuir adsorption isotherm parameters for As (III) and As (V) with thiomer Initial concentration (ppm) As (III) As (V) qm (mg/g) KL R2 RL qm (mg/g) KL R2 RL 1.0 0.89 0.008 0.998 0.98 0.93 0.0396 0.999 0.93 6 0.94 0.003 0.999 0.98 2.44 0.0039 0.999 0.97 18 8.4 0.012 0.999 0.81 4.87 0.0192 0.996 0.7 30 13.02 0.007 0.999 0.77 11.75 0.003 0.999 0.9 60 25.96 0.008 0.999 0.51 25.45 0.015 0.999 0.09 Langmuir adsorption isotherm parameters for As (III) and As (V) with sulfonium 1.0 0.75 0.36 0.999 0.27 0.9 0.0024 0.998 0.99 6 2.1 0.009 0.999 0.95 2.12 0.0065 0.999 0.97 18 6.85 0.005 0.998 0.89 6.82 0.025 0.999 0.85 30 9.5 0.013 0.999 0.95 14.22 0.031 0.999 0.90 60 28.64 0.007 0.987 0.58 25.62 0.004 0.998 0.64 Table 3: Freundlich adsorption isotherm parameters. Freundlich adsorption isotherm parameters for As (III) and As (V) with thiomer Initial concentration (ppm) As (III) As (V) kf (mg/g) 1/n R2 kf (mg/g) 1/n R2 1 0.7 0.87 0.998 0.73 0.99 0.998 Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 8 6 1.08 0.38 0.969 1.36 0.39 0.969 18 0.8 0.87 0.998 0.93 0.99 0.998 30 0.74 0.92 0.997 0.74 0.81 0.997 60 0.69 0.94 0.991 0.73 0.73 0.998 Freundlich adsorption isotherm parameters for As (III) and As (V) with sulfonium 1 0.7 0.7 0.998 0.73 0.99 0.997 6 0.74 0.98 0.997 0.75 0.98 0.996 18 0.66 0.93 0.972 1.08 0.99 0.998 30 0.68 0.95 0.996 0.76 0.98 0.997 60 0.74 0.97 0.998 0.93 0.99 0.998 Kinetic studies To understand the process of adsorption of As (III) and As (V) onto starch derivatives, the pseudo-first and pseudo-second order were analyzed. The kinetic models help to understand the mechanism of sorption on the surface of the adsorbent. The pseudo first order model is expressed as. Where qe (mg g-1) and qt (mg g-1) are the adsorption amount at equilibrium and at time t, respectively and k1 (min-1) is the pseudo first order rate constant. The values of the adsorption rate constant (k1) for the sorbents at different initial arsenic concentrations were obtained from slopes of the plots of log (qe-qt) versus time. The pseudo second order model is expressed as. Where, k2 (g (mg min-1)) is the pseudo-second-order rate constant. The kinetic results depict that pseudo-first-order for arsenic sorption diverges from linearity with a lower correlation coefficient (R2) value in comparison to the pseudo second order model. Therefore, the best suitability of the kinetic data corresponds to the pseudo-second-order model for the entire adsorption period. The suitability of pseudo-second order model, which is based on the possibility of chemisorption confirms the electrostatic attraction between the adsorbents and adsorbate. Thus, the correlation coefficient (R2) has the highest value for the pseudo-secondorder model (Table 4). Table 4: Pseudo-first-order and second-order kinetic parameters for As (III) and as (V) sorption via thiomer and sulfonium starch. Pseudo-first-order kinetic parameters CO (ppm) As (III) with thiomer As (V) with thiomer As (III) with sulfonium As (V) with sulfonium qe K2 R2 qe K2 R2 qe K2 R2 qe K2 R2 1 0.51 0.01 0.7062 0.38 0.004 0.7146 0.45 0.006 0.8476 0.52 0.0059 0.8476 6 0.93 0.004 0.9405 0.92 0.005 0.8527 0.78 0.005 0.9811 0.85 0.0057 0.9372 18 1.65 0.003 0.7825 2 0.005 0.9082 1.62 0.006 0.8995 4 0.0059 0.9013 30 2.8 0.465 0.9574 2.57 0.778 0.9832 2.75 0.004 0.9531 2.8 0.0043 0.9636 60 3.21 0.001 0.9355 3.38 0.003 0.968 3.05 0.003 0.9618 4 0.0069 0.9013 Pseudo-second-order kinetics parameters 1 0.17 0.21 0.9996 0.344 0.41 0.9997 0.262 0.338 0.9979 0.111 0.14 0.9976 6 1.13 0.024 0.995 0.016 0.015 0.9984 0.029 0.003 0.9951 0.012 0.023 0.9954 18 0.23 0.006 0.9987 0.228 0.027 0.999 0.233 0.009 0.9985 0.249 0.075 0.9994 30 0.49 0.002 0.9939 2.37 0.001 0.9956 0.242 0.001 0.9471 0.199 0.001 0.9946 60 0.26 0.001 0.988 1.01 0.002 0.9915 0.136 0.002 0.9724 0.81 0.002 0.9925 Vishal Priya Der Pharma Chemica, 2023, 15(5): 1-13 9 Sorption characterization by SEM-EDX Microphotographs of modified thiol starch, sulfonium starch, iron immobilized thiomer and iron immobilized sulfonium starch were obtained in support of the sorption study (Figure 10). From the SEM images, it is evident that thiol starch and sulfonium starch possess heterogeneous surfaces due to small out-growths. This surface roughness in starch derivatives may probably be useful in arsenic sorption from aqueous solutions. After arsenic sorption thiol starch and sulfonium starch adsorbents surface is attaining smoothness. It is clear from the increased smoothness of the matrix surface and decrease in the porosity distance that the absorbed arsenic species are aggregated on the surface of sulfonium and thiomer products. The significant deformation in the structural organization of the starch derivative safer sorption is an attribute towards the high adsorption of arsenic on the adsorbent surface (Figure 10). Figure 10: Effect of competitive ions on percent uptake of (a) As (III) via iron immobilized thiomer (b) As (V) via iron immobilized thiomer (c) As (III) via iron immobilized sulfonium and (d) As (V) via iron immobilized sulfonium. On other hand, there is remarkable change in the morphology and structure when the iron is incorporated on thiol starch and sulfonium starch and this accounts the binding of iron with thiolated starch and sulfonium starch. The SEM images show some white spots and out-growths on the surface of iron loaded thiolated starch and iron loaded sulfonium starch which indicate the sorption of arsenic. Furthermore, EDS analysis also supports the sorption. The results clearly show the presence of arsenic on the surfaces of thiol starch and sulfonium starch (Figure 11). The EDS analysis of sulfoniumm and thiomerm have major component Fe (17.86% and 7.14%) iron content was also observed. Upon immobilization of Fe on starch derivatives surface, there is an increase in iron percentage and adsorption of arsenic onto the surface of iron coated thiomerm and sulfoniumm showed the presence of As (III) and As (V) upto a maximum concentration of iron increased upto 8.83%, 51.98%, 12.81% and 60.86% (Figure 13) compared to precursor (Figure 12), which indicates significant adsorption of arsenic on to the surface of polymer (Figures 11-13).