Synthesis and reactivity of a trigonal porous nanographene on a gold surface

Synthesis and reactivity of a trigonal porous nanographene on a gold surface† Rafal Zuzak, a Iago Pozo, b Mads Engelund, c Aran Garcia-Lekue, de Manuel VilasVarela, b Jos´ e M. Alonso, b Marek Szymonski, a Enrique Guiti´ an, b Dolores P´ erez, b Szymon Godlewski * a and Diego Pe˜ na * b The synthesis of porous nanographenes is a challenging task for solution chemistry, and thus, on-surface synthesis provides an alternative approach. Here, we report the synthesis of a triporous nanographene with 102 sp 2 carbon atoms by combining solution and surface chemistry. The carbon skeleton was obtained by Pd-catalyzed cyclotrimerization of arynes in solution, while planarization of the molecule was achieved through two hierarchically organized on-surface cyclodehydrogenation reactions, intraand inter-blade. Remarkably, the three non-planar [14]annulene pores of this nanographene further evolved at higher temperatures showing interesting intra-porous on-surface reactivity. Introduction Recently, nanographenes have attracted much attention in materials sciences due to their unique optoelectronics properties. 1 This interest has motivated the search for efficient methods to prepare well-dened nanographenes by chemical synthesis. In particular, nanographenes with embedded pores in their structure are specially interesting materials, since the pores can signicantly inuence the electronic properties of these graphene derivatives. In addition, porous graphenes can be used in a large variety of applications, including sequencing, gas separation and sieving. However, the available synthetic methodologies to prepare well-dened porous nanographenes are quite limited. 2–4 In this respect, an interesting approach is the combination of solution and on-surface chemistry. 5,6 For example, this strategy has recently allowed the bottom–up preparation of a multifunctional nanoporous graphene. 7 Very recently, M¨ ullen, Fasel, Feng and co-workers reported on the preparation of a porous nanographene with 78 sp 2 carbon atoms by the on-surface cyclodehydrogenation of a starphene derivative through the formation of three C–C bonds (Fig. 1). 8 Concurrently, we envisioned the synthesis of the related porous nanographene 1, with 102 sp 2 carbon atoms and three non-planar [14]annulene pores within its structure. We plan to obtain this nanographene starting with dodecaphenyl[7] starphene 2, which could be easily obtained by means of aryne chemistry in solution. 9 Then, sequential on-surface cyclodehydrogenations through the formation of nine intra-blade C–C bonds (in blue) and three inter-blade C–C bonds (in red) would afford trigonal porous nanographene 1. Results and discussion We started the synthetic route by preparing triate 3(Fig. 2), which should be an adequate precursor of aryne 4(ESI†for Fig. 1 Structures of two porous nanographenes with three embedded [14]annulene pores. a Centre for Nanometer-Scale Science and Advanced Materials, NANOSAM, Faculty of Physics, Astronomy and Applied Computer Science, Jagiellonian University, Łojasiewicza 11, PL 30-348 Krak´ ow, Poland. E-mail: szymo[email protected] b Centro de Investigaci´ on en Qu´ ımica Biol´ oxica e Materiais Moleculares (CiQUS), Departamento de Qu´ ımica Org´ anica, Universidade de Santiago de Compostela, 15782-Santiago de Compostela, Spain. E-mail: diego.p[email protected] c Espeem S.A.R.L., L-4365 Esch-sur-Alzette, Luxembourg d Donostia International Physics Center, DIPC, Paseo Manuel de Lardizabal 4, E-20018 Donostia-San Sebasti´ an, Spain e IKERBASQUE, Basque Foundation for Science, E-48013 Bilbao, Spain †Electronic supplementary information (ESI) available. See DOI: 10.1039/c9sc03404h Cite this: Chem. Sci.,2019,10,10143 All publication charges for this article have been paid for by the Royal Society of Chemistry Received 9th July 2019 Accepted 13th September 2019 DOI: 10.1039/c9sc03404h rsc.li/chemical-science This journal is © The Royal Society of Chemistry 2019 Chem. Sci.,2019,10,10143–10148 | 10143 Chemical Science EDGE ARTICLE Open Access Article. Published on 13 September 2019. Downloaded on 4/13/2020 4:39:06 PM. This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. View Article Online View Journal | View Issue details). According to our well-established methodology for the palladium-catalyzed cyclotrimerization of arynes, 9d subsequent generation of aryne 4by uoride-induced decomposition of triate 3in the presence of Pd(PPh 3 ) 4 led to the isolation of dodecaphenyl[7]starphene 2in 37% yield. Then, we attempted the preparation of porous nanographene 1by DDQ-promoted cyclodehydrogenation of compound 2in solution. Unfortunately, this approach was unsuccessful since we only detected the formation of nanographene 5as the result of nine intrablade cyclodehydrogenations. Based on our recent experience, 10 we attempted the preparation of 1by on-surface cyclodehydrogenation of 5through inter-blade C–C bond formation. However, the deposition of compound 5on a gold surface by sublimation from an effusion cell proved to be infeasible, most probably due to signicant intermolecular interactions. Then, we decided to study sequential on-surface cyclodehydrogenations of trimer 2as explained below. Aer thermal deposition of precursors 2on Au(111), we found that these molecules tend to gather into disordered pstacked assemblies, whose structures are difficult to determine by STM. This is due to the high degree of conformational exibility due to the rotation of the peripheral phenyl rings. This exibility combined with the steric hindrance between neighboring phenyl rings leads to the molecules adopting a nonplanar geometry. On a metal surface, which is known to catalyse cyclodehydrogenation reactions, 11 intramolecular fusion between neighboring phenyl rings shall occur. Intuitively, at rst we might envision ring closure between phenyls attached to the very same naphthalene moiety of the molecule core (intra-blade). This would transform trinaphthylene 2into the polycyclic three-bladed propeller 5. Each of the wide propeller blades would be then composed of 9 rings. It is instructive to note that the transformed molecule would retain the non-planar character due to the steric interactions between the outermost rings of neighboring propeller blades within the necking of the conjoined bay regions. Indeed, annealing at 300–340 C induced considerable modication of STM images: the disordered assemblies were gone and we found the molecules as individual entities dispersed over the surface area. Closer inspection of the recorded STM images led to the conclusion that compound 5was formed as the major reaction product (Fig. 3a). In fact, the individual molecules were recorded as triangular objects with rounded vertices, while their internal contrast was nonuniform. The STM images showed three bright lobes, each located within one of the longer molecule edges as clearly discernible in Fig. 3a. Simple comparison between the anticipated shape of compound 5and the STM topographies suggested that the lobes appearing bright may correspond to the necking of the conjoined bay regions, where the steric hindrance led to out-of-plane dent of the neighboring propeller blades. The appearance of three bright lobes might be thus associated with the repulsive steric interaction between each pair of propeller blades and consequently also their bending. Minor differences among the recorded STM topographies of the molecules, expressed mainly in the details of the bright lobes' location and intensities, might be associated with differences in geometrical conformation. These differences arose from the opposite bending directions of neighboring propeller blades surrounding the conjoined bay region in 5. Such a process shall occur within each pair of propeller blades giving rise to numerous stereoisomers with pairs of blades differently bent and consequently providing a variety of slightly different STM images. Fig. 2 Synthetic route to obtain porous nanographene 1. Fig. 3 Products detected after thermal annealing of trinaphthalene 2 on Au(111); (a) filled state STM image of molecules 5obtained after annealing of precursor 2at 300 C, which led to intra-blade cyclodehydrogenation and formation of intermediate 5; the inset shows the STM topography of a single molecule 5with three clearly discernible bright protrusions marked with dashed yellow circles; (b) filled state STM image of molecules obtained after precursor annealing at 370 C; green, yellow and blue circles denote molecules with two, one and no bright protrusions in STM images, respectively; (c–e) high resolution filled state STM images of molecules 6,7and 1obtained after annealing at 370 C drawn together with anticipated structural schemes (f–h); color coding identical to that in panel (b), new C–C bonds closing [14]annulene pores are highlighted in red within (f–h) schemes; imaging parameters: tunnelling current 100 pA, bias voltage 1.0 V. 10144 |Chem. Sci.,2019,10,10143–10148 This journal is © The Royal Society of Chemistry 2019 Chemical Science Edge Article Open Access Article. Published on 13 September 2019. Downloaded on 4/13/2020 4:39:06 PM. This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. View Article Online Further transformation of compound 5was achieved when the annealing temperature was slightly raised to the range of approximately 340–380 C. The molecules were still distributed over the surface and their STM images retained a triangular shape; however, the internal contrast was different. We noticed that unlike in the case of lower temperature annealing, now we could not detect molecules exhibiting 3 bright lobes (compound 5) as documented in Fig. 3b. Instead, the molecules could be classied into three co-existing groups depending on the number of bright lobes recorded for a single molecule. They are visualized in Fig. 3c–e. The rst group (Fig. 3c) contained only one bright lobe, the second family exhibited two bright lobes (Fig. 3d) and the last third one gathered molecules which do not exhibit any bright protrusion (Fig. 3e). The latter group could be characterized by a three-fold symmetric appearance with a slightly brighter Y-shape in the centre indicating the successful generation of porous nanographene 1. The above described observations suggested that at 340–380 C inter-blade fusion between neighboring propeller blades of the intermediate compound 5was initiated. The formation of a single C–C bond between peripheral benzene rings of neighboring propeller blades resulted in a partial planarization, closure of conjoint bay regions and disappearance of the bright lobe in STM images. The presence of molecules exhibiting two (Fig. 3d), one (Fig. 3c) or zero (Fig. 3e) bright lobes in STM topographies might be linked with the formation of one (compound 7, Fig. 3g), two (compound 6, Fig. 3f) or three [14]annulene rings (compound 1, Fig. 3h) within a single molecule, respectively. Such an interpretation seems to be plausible; however, one cannot denitely prove this scenario based solely on STM images of the molecules. In order to dispel doubts we decided to apply nc-AFM imaging with CO functionalized tips allowing for bond resolved analysis of the molecule internal architecture. 12 As the molecules exhibiting three bright lobes (compound 5) were expected to exhibit a severe non-planar structure, we decided to inspect compound 7with at greatest two maxima. Imaging at an elevated height conrmed that the bright lobes in STM images came from the signicant non-planarity of the molecules (ESI Fig. S4†). We next turned to the molecule with only one bright lobe and anticipated two incorporated [14] annulene units (compound 6, Fig. 4a and b). The nc-AFM measurement with CO-functionalized tip immediately conrmed the generation of two new C–C bonds between neighboring propeller blades, which led to the closure of two conjoint bay regions of necking and the formation of two fourteen-membered rings as highlighted in red in Fig. 4c and d. The nc-AFM image exhibited a much brighter appearance of the newly created bonds thus revealing the geometrical conformation of the molecule on the surface. It turned out that the central part of the molecule was located much closer to the surface area, while the carbon atoms located at the outskirts of the nanographene ake –which form the new bonds and, consequently, the [14]annulene rings –were raised above the central ring plane. This resulted from the steric hindrance between the hydrogen atoms pointing toward the center of the fourteen-membered ring pore, in agreement with a recent report for the smaller porous nanographene C78 (Fig. 1). 8 Similar observations could also be made for the target Fig. 4 STM and nc-AFM images of compounds 6and 1; (a and b) filled state STM and frequency shift nc-AFM images of a molecule with one bright lobe; the AFM image confirms that the bright protrusion in the STM image corresponds to the geometrically elevated part of compound 6; (c) Laplace-filtered bond-resolved frequency shift nc-AFM image of a flat part of molecule 6indicated by red rectangles in (a and b) demonstrating the formation of two new C–C bonds (red dashed ovals) between neighboring propeller blades; (d) structure of compound 6with new bonds highlighted in red; (e and f) filled state STM and Laplace-filtered bond resolved frequency shift nc-AFM images of nanographene 1; (g) structure of compound 1with new bonds highlighted in red; imaging conditions: tunnelling current 100 pA, bias voltage 1.0 V. This journal is © The Royal Society of Chemistry 2019 Chem. Sci.,2019,10,10143–10148 | 10145 Edge Article Chemical Science Open Access Article. Published on 13 September 2019. Downloaded on 4/13/2020 4:39:06 PM. This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. View Article Online nanographene 1, which did not exhibit any bright lobes in the STM image (Fig. 4e). The nc-AFM frequency shiimage shown in Fig. 4f nally proved the generation of the three-fold symmetric non-planar porous nanographene 1with three [14] annulene rings embedded (Fig. 4g). Remarkably, the central triphenylene core of the molecule appeared closer to the surface compared to the rest of the molecule. Having conrmed the synthesis of porous nanographene 1, we analysed its electronic structure by means of scanning tunneling spectroscopy (STS). Fig. 5 shows spatial maps of electron clouds acquired at voltages corresponding to resonances registered in single point dI/dVcurves (see the ESI, Fig. S5†). These images are plotted together with the simulated constant current dI/dVmaps exhibiting reasonable conformity. Slight deviations may be attributed to the details of the molecular geometrical conformation and the microscope tip apex structure. Mixing of different molecular orbitals especially for deeper lying states may also play a role. 13 Due to the large size of the nanographene, full computational analysis of its conformation upon adsorption on Au(111) would require very costly calculations. Moreover, the molecules are expected to interact weakly with the substrate, as demonstrated by the negligible orbital hybridization previously reported for other hydrocarbons. 10,14 Consequently, we decided to perform rst principles calculations without the explicit incorporation of the surface, as described in detail in the ESI (Fig. S7†). The overall good consistency of calculated and experimental dI/dVmaps conrms the validity of the applied approximation. Interestingly, further increase of the annealing temperature could be used for initiation of new transformations within the [14]annulene pores of nanographene 1, as shown in Fig. 6. The lled state STM image clearly shows lowering of the image symmetry and the appearance of a dark shadow close to one of the edges (Fig. 6a). The corresponding bond-resolved nc-AFM image (Fig. 6c) allows the unravelling of the new structure (compound 8, Fig. 6b and ESI Fig. S8†). A closer look indicated that the molecule became completely asymmetric since the three pores evolved differently. In particular, one of the 14membered rings underwent two cyclodehydrogenations and transforms into a moiety containing two pentagonal rings fused to an eight-membered ring (marked in blue in Fig. 6d). A second [14]annulene underwent only one cyclodehydrogenation resulting in the formation of a pentagonal ring fused to an eleven-membered ring (highlighted in purple in Fig. 6d). The transformation analysis of the third [14]annulene ring led to even more surprising conclusions. This is because the nc-AFM image of this part still exhibited a symmetric appearance, however, with a bright protrusion located in the middle and four noticeable elongated features connecting the central lobe Fig. 5 Calculated and experimental constant current dI/dVimages of compound 1acquired at voltages corresponding to resonances in single point STS data (see the ESI, Fig. S5 and S7†); (a) calculated (upper panel) and experimental (lower panel) filled state dI/dVmaps corresponding to HOMO-2, HOMO-1 and HOMO states; (b) calculated (upper panel) and experimental (lower panel) filled state dI/dVmaps corresponding to LUMO, LUMO+1 and LUMO+2 states; for molecular orbital analysis please refer to the ESI, Fig. S5 and S7.† Fig. 6 Compound 8, detected after subjecting nanographene 1to thermal annealing at 415 C; (a) high resolution filled state STM topography with two clearly visible slight depressions and one darker depression; (b) anticipated structural (gas phase relaxed) model of the molecule shown in (a) exhibiting reduced symmetry compared to molecules heated up to 370 C (for details see main text and Fig. S8†); (c and d) Laplace-filtered bond-resolved frequency shift nc-AFM images of the molecule shown in (a), and in panel (d) differences with the molecule containing three [14]annulene units are highlighted; red lines indicate non-modified C–C bonds; blue lines show two [14] annulene pores transformed into the two following units: one containing two pentagonal rings and one octagonal, the second unit built from an undecagonal ring with a pentagonal one attached; green lines indicate the anticipated bonds between the carbon atoms from the third [14]annulene ring and the Au adatom located in the center; imaging parameters: tunnelling current 50 pA, bias voltage 1.0 V. 10146 |Chem. Sci.,2019,10,10143–10148 This journal is © The Royal Society of Chemistry 2019 Chemical Science Edge Article Open Access Article. Published on 13 September 2019. Downloaded on 4/13/2020 4:39:06 PM. This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. View Article Online with the surrounding carbon atoms. Such an appearance resembled the presence of an additional atom attached to four C atoms from the 14-membered ring pore. We interpret this additional feature as the manifestation of an Au adatom capture within the pore similar to the self-metalation of porphyrin molecules, 15 which depending on the oxidation state might exhibit a depression around the additional atom. 16 The square planar molecular geometry of this cycloaurated structure suggests the formation of an Au(III) complex with a formal negative charge on the gold atom (ESI Fig. S8†). 17 Gas phase calculations of compound 8conrmed the stability of the proposed structure (Fig. 6b), hence predicting signicant distortion from the planar conformation mainly due to the steric interactions within the 11-membered ring. The recorded nc-AFM image indicated a less distorted geometrical conguration, which may originate from the inuence of the underlying substrate. Conclusions In conclusion, by combining solution chemistry with sequential on-surface reactions, we have synthesized a non-planar threefold porous nanographene with [14]annulene units embedded. The structure of the target nanographene and the corresponding intermediates has been analysed in detail by means of combined nc-AFM and STM experiments, and the porous nanographene electronic structure has been visualized by STM/STS measurements corroborated by theoretical modelling. The specically designed precursor, consisting of three centrally fused branches with twelve peripheral phenyl rings, allowed on-surface intra-branch cyclodehydrogenation leading to the formation of a three-blade propeller. The following second-step cyclodehydrogenation processes nally led to the porous nanographene by closing fourteen-membered rings. Overall, twelve new C–C bonds accompanied by nine benzene rings and three [14]annulene pores were generated. By this we set a new path for the synthesis of large exotic nanographenes, where a single-step cyclodehydrogenation is not sufficient for their formation. Finally, we have explored the reactivity of these 14-membered ring pores on a gold surface by visualizing three different transformations within the same nanographene. Conflicts of interest There are no conicts to declare. Acknowledgements We thank F. L´ opez for fruitful discussions. We acknowledge nancial support from the National Science Center, Poland (2017/26/E/ST3/00855), Agencia Estatal de Investigaci´ on (MAT2016-78293-C6-3-R and CTQ2016-78157-R), Xunta de Galicia (Centro singular de investigaci´ on de Galicia, accreditation 2016–2019, ED431G/09) and Fondo Europeo de Desarrollo Regional (FEDER). IP thanks Xunta de Galicia and the European Union (European Social Fund, ESF) for awarding a pre-doctoral fellowship. Notes and references 1(a) F. Bonaccorso, Z. Sun, T. Hasan and A. C. Ferrari, Nat. Photonics, 2010, 4, 611–622; (b) O. Ostroverkhova, Chem. Rev., 2016, 116, 13279–13412. 2 U. Beser, M. Kastler, A. Maghsoumi, M. Wagner, C. Castiglioni, M. Tommasini, A. Narita, X. Feng and K. M¨ ullen, J. Am. Chem. Soc., 2016, 138, 4322–4325. 3(a) K. Ikemoto, R. Kobayashi, S. Sato and H. Isobe, Angew. Chem., Int. Ed., 2017, 56, 6511–6514; (b) L. He, C. Ng, Y. Li, Z. Liu, D. Kuck and H. Chow, Angew. Chem., Int. Ed., 2018, 57, 13635–13639. 4 J. C. Buttrick and B. T. King, Chem. Soc. Rev., 2017, 46,7–20. 5 J. Hieulle, E. Carbonell-Sanrom` a, M. Vilas-Varela, A. GarciaLekue, E. Guiti´ an, D. Pe˜ na and J. I. Pascual, Nano Lett., 2018, 18, 418–423. 6(a) M. Ammon, T. Sander and S. Maier, J. Am. Chem. Soc., 2017, 139, 12976–12984; (b) M. Bieri, M. Nguyen, O. Gr¨ oning, J. Cai, M. Treier, K. A¨ ıt-Mansour, P. Ruffieux, C. A. Pignedoli, D. Passerone, M. Kastler, K. M¨ ullen and R. Fasel, J. Am. Chem. Soc., 2010, 132, 16669–16676; (c) M. Bieri, M. Treier, J. Cai, K. A¨ ıt-Mansour, P. Ruffieux, O. Gr¨ oning, P. Gr¨ oning, M. Kastler, R. Rieger, X. Feng, K. M¨ ullen and R. Fasel, Chem. Commun., 2009, 6919–6921. 7 C. Moreno, M. Vilas-Varela, B. Kretz, A. Garcia-Lekue, M. V. Costache, M. Paradinas, M. Panighel, G. Ceballos, S. O. Valenzuela, D. Pe˜ na and A. Mugarza, Science, 2018, 360, 199–203. 8 K. Xu, J. I. Urgel, K. Eimre, M. Di Giovannantonio, A. Keerthi, H. Komber, S. Wang, A. Narita, R. Berger, P. Ruffieux, C. A. Pignedoli, J. Liu, K. M¨ ullen, R. Fasel and X. Feng, J. Am. Chem. Soc., 2019, 141, 7726–7730. 9(a) J. M. Alonso, A. E. D´ ıaz-´ Alvarez, A. Criado, D. P´ erez, D. Pe˜ na and E. Guiti´ an, Angew. Chem., Int. Ed., 2012, 51, 173–177; (b) B. Schuler, S. Collazos, L. Gross, G. Meyer, D. P´ erez, E. Guiti´ an and D. Pe˜ na, Angew. Chem., Int. Ed., 2014, 53, 9004–9006; (c) M. Vilas-Varela, S. Fatayer, Z. Majzik, D. P´ erez, E. Guiti´ an, L. Gross and D. Pe˜ na, Chem.–Eur. J., 2018, 24, 17697–17700; (d)D.Pe ˜ na, S. Escudero, D. P´ erez, E. Guiti´ an and L. Castedo, Angew. Chem., Int. Ed., 1998, 37, 2659–2661. 10 R. Zuzak, J. Castro-Esteban, P. Brandimarte, M. Engelund, A. Cobas, P. Piatkowski, M. Kolmer, D. P´ erez, E. Guiti´ an, M. Szymonski, D. S´ anchez-Portal, S. Godlewski and D. Pe˜ na, Chem. Commun., 2018, 54, 10256–10259. 11 (a)K.Weiss,G.Beernink,F.D ¨ otz, A. Birkner, K. M¨ ullen and C. H. W¨ oll, Angew. Chem., Int. Ed., 1999, 38, 3748–3752; (b) J. Cai, P. Ruffieux,R.Jaafar,M.Bieri,T.Braun, S. Blankenburg, M. Muoth, A. P. Seitsonen, M. Saleh, X. Feng, K. M¨ ullen and R. Fasel, Nature, 2010, 466, 470–473; (c) M. Treier, C. A. Pignedoli, T. Laino, R. Rieger, K. M¨ ullen, D. Passerone and R. Fasel, Nat. Chem., 2010, 3,61–67. 12 L. Gross, F. Mohn, N. Moll, P. Liljeroth and G. Meyer, Science, 2009, 325, 1110–1114. 13 W. H. Soe, C. Manzano, A. De Sarkar, N. Chandrasekhar and C. Joachim, Phys. Rev. Lett., 2009, 102, 176102–176104. This journal is © The Royal Society of Chemistry 2019 Chem. Sci.,2019,10,10143–10148 | 10147 Edge Article Chemical Science Open Access Article. Published on 13 September 2019. Downloaded on 4/13/2020 4:39:06 PM. This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. View Article Online 14 R. Zuzak, R. Dorel, M. Krawiec, B. Such, M. Kolmer, M. Szymonski, A. M. Echavarren and S. Godlewski, ACS Nano, 2017, 11, 9321–9329. 15 (a) A. Kretschmann, M.-M. Walz, K. Flechtner, H.-P. Steinr¨ uck and J. M. Gottfried, Chem. Commun., 2007, 568–570; (b) R. Gonz´ alez-Moreno, C. S´ anchez-S´ anchez, M. Trelka, R. Otero, A. Cossaro, A. Verdini, L. Floreano, M. Ruiz-Bermejo, A. Garc´ ıa-Lekue, J. A. Mart´ ın-Gago and C. Rogero, J. Phys. Chem. C, 2011, 115, 6849–6854; (c) K. Diller, F. Klappenberger, M. Marschall, K. Hermann, A. Nefedov, Ch. W¨ oll and J. V. Barth, J. Chem. Phys., 2012, 136, 014705. 16 (a)S.M ¨ ullegger, W. Sch¨ oerger, M. Rashidi, L. M. Reith and R. Koch, J. Am. Chem. Soc., 2009, 131, 17740–17741; (b) S. M¨ ullegger, M. Rashidi, W. Sch¨ oerger and R. Koch, Surf. Sci., 2018, 678, 157–162. 17 M. A. Bennett, D. C. R. Hockless, A. D. Rae, L. L. Welling and A. C. Willis, Organometallics, 2001, 20,79–87. 10148 |Chem. Sci.,2019,10,10143–10148 This journal is © The Royal Society of Chemistry 2019 Chemical Science Edge Article Open Access Article. Published on 13 September 2019. Downloaded on 4/13/2020 4:39:06 PM. This article is licensed under a Creative Commons Attribution 3.0 Unported Licence. View Article Online