Photoredox Heterobimetallic Dual Catalysis Using Engineered Covalent Organic Frameworks

Photoredox Heterobimetallic Dual Catalysis Using Engineered Covalent Organic Frameworks Alberto López-Magano, Borja Ortín-Rubio, Inhar Imaz, Daniel Maspoch, JoséAlemán,* and Rubén Mas-Ballesté* Cite This: ACS Catal. 2021, 11, 12344−12354 Read Online ACCESS Metrics & More Article Recommendations * sıSupporting Information ABSTRACT: The functionalization of an imine-based layered covalent organic framework (COF), containing phenanthroline units as ligands, has allowed the obtention of a heterobimetallated material. Photoactive Ir and Ni fragments were immobilized within the porous structure of the COF, enabling heterogeneous light-mediated Csp3−Csp2cross-couplings. As radical precursors, potassium benzyland alkoxy-trifluoroborates, organic silicates, and proline derivatives were employed, which brings out the good versatility of Ir,Ni@Phen-COF. Moreover, in all the studied cases, an enhanced activity and stability have been observed in comparison with analogous homogenous systems. KEYWORDS: covalent organic frameworks, photocatalysis, dual catalysis, C−C bond formation, heterogeneous catalysis 1. INTRODUCTION Carbon−carbon couplings are one of the most useful and important transformations in modern chemistry. 1 They include classical cross-coupling reactions, 2 such as Suzuki, Sonogashira, and olefin metathesis; 3 some of them recognized with the Nobel prize. 4 The importance of these reactions relies on their key role in the synthesis of pharmaceutical drugs, construction of complex molecules, and late stage functionalizations. However, there is still a need of searching new synthetic methodologies with high functional group tolerance, in which are included new Csp3−Csp2bonds. In this sense, photocatalytic reactions have appeared as a new tool in the last decade, solving some of the problems associated with the formation of C−C bonds under mild reaction conditions. 5 Among them, photoredox Ir−Ni dual catalysis has become an outstanding solution (top, Figure 1). 5 In this reaction, two well-distinguished and connected catalytic cycles are combined: first, the Ir photocatalyst generates a radical intermediate under light irradiation; and second, the Ni species mediates in the formation of the new C−C bond. 6,7 Although this is a very powerful methodology, Ir−Ni dual photocatalysis also suffers of some general drawbacks. First, iridium is an expensive metal center and its recyclability in the homogeneous system is difficult, 8 increasing the costs of these processes. Furthermore, Ni sources commonly undergo deactivation in the presence of light, oxygen, or organic reactive species, giving rise to the formation of unreactive agglomerated Ni/NiO nanoparticles. This hampers the furtherance of the reaction, leading to lower yields and turnover numbers (TONs). 9 Therefore, a plausible strategy to overcome the limitations of homogenous Ir−Ni dual catalysis would consist of the design of heterogeneous systems. The use of catalytic heterogeneous materials allows their easy separation from the reaction medium. In addition, the immobilization and isolation of catalytically active sites may enhance their stability and reactivity, due to the hampering of unproductive encounters or deactivation pathways, 10 such as the formation of inactive agglomerated Ni/NiO nanoparticles. 9 Besides, cooperative phenomena between distinct isolated catalytic centers can be enhanced by the control of proximity in predetermined sites on the material. To this end, it would be a feasible strategy to immobilize molecular metallic catalytic sites into porous materials, such as covalent organic frameworks (COFs). 11,12 This family of materials is in its heyday on their catalytic applications. 13 They constitute a class of crystalline and porous reticular materials formed by the assembly of covalent bonds of different nature. 14 Among them, imine-based COFs have attracted a good deal of attention, due to their stability, availability of the constituting building blocks, and the easy isolation of crystalline and porous structures under mild reaction conditions. 15,16 The accessibility Received: August 11, 2021 Revised: September 9, 2021 Published: September 21, 2021 Research Articlepubs.acs.org/acscatalysis © 2021 American Chemical Society 12344 https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 Downloaded via CSIC on March 29, 2022 at 11:11:31 (UTC). See https://pubs.acs.org/sharingguidelines for options on how to legitimately share published articles. Figure 1. Previous works and the conceptual strategy of this work. Scheme 1. Synthesis of Phen-COF ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12345 to a variety of building blocks allows the design of COFs containing different functional units in their framework. 17 In particular, some COFs have been isolated containing donor groups (e.g., bipyridine, 18 salen, 19 porphyrin, 20 or catechol, 21 among others) 19,22−24 that can act as ligands toward a variety of metal centers. As a result, different organic transformations have been achieved with a variety of metals. 17,22,23,25 However, dual bimetallic photocatalytic processes are a challenging goal that never have been tackled with this family of materials. In particular, dual catalytic systems require a high level of synchronicity between the two catalytic sites, because the intermediates involved in such processes are very reactive and not isolable. The proximity and cooperativity between the distinct catalytic sites are a key issue in the design of a dual catalytic process, and therefore catalytic sites must work in close proximity. 26 Regarding this issue, two pioneering works using metal organic frameworks (MOFs) have reported the isolation of Ni and Ir centers through coordination to bipyridine fragments, achieving dual photocatalytic processes. 27,28 In addition, nonporous amorphous linear polymers designed with pending arms containing bipyridine fragments have also been used for Figure 2. Characterization of Phen-COF. (A) SEM image; (B) PXRD simulated and experimental pattern; (C) FT-IR spectra; (D) 13C NMRCPMAS spectrum; (E) adsorption−desorption N2isotherm; and (F) thermogravimetric analysis. ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12346 these purposes. 29 Inspired by these precedents, this work is intended to design a bimetallated COF that requires simple synthetic procedures and to obtain a very stable and active material. In particular, we immobilize Ir and Ni fragments into phenanthroline units in a new imine-based COF (hereafter called Phen-COF), allowing the interplay of both catalytic metal centers for the formation of Csp3−Csp2bonds (bottom, Figure 1). This heterogeneous strategy permits the improvement of the catalytic performance compared with the homogeneous version of the coupling reaction. 2. RESULTS AND DISCUSSION 2.1. Synthesis and Characterization. Phen-COF was prepared by combining the symmetric building block 1, which contains a centered phenanthroline unit and two aldehyde groups located at its ends, and the well-known triamine 1,3,5tris(4-aminophenyl)benzene (TAPB) (see Scheme 1). 12 First, the dialdehyde 1was made by a double Suzuki−Miyaura crosscoupling between 3,8-dibromo-1,10-phenanthroline and 4formylphenylboronic acid. Then, a screening of typical conditions for the synthesis of Phen-COF was performed. In most of the cases, a yellow amorphous material was obtained (see Table S1 of Supporting Information), probably because of the poor solubility of phenanthroline building block 1. Interestingly, using a mixture of 9:1 (v/v) of mesitylenedioxane and 6 M acetic acid on a sealed solvothermal reactor, we were able to isolate a material with moderate crystallinity after 3 days at 120 °C (entry 15, Table S1). Longer reaction times, higher temperatures, or the use of acid catalysts of different nature did not improve the crystallinity of the material, not even post-thermal annealing treatments or activation with supercritical CO2. Field-emission scanning electron microscopy (FE-SEM) of the resulting yellow powder revealed the formation of a layered-type COF (Figure 2A). The formation of the expected layered polyimine structure of Phen-COF (Scheme 1) was first confirmed by powder X-ray diffraction (PXRD) (Figure 2B). Using the Materials Studio 8.0 Program, we compared this experimental PXRD data with the pattern simulated from the analogous layered, eclipsed structure of PI-COF-3 previously reported by Yan et al. 30 Based on this structure, we applied a geometrical energy minimization using the universal force field. The unit cell parameters found for the layered eclipsed structure were a= 3.52 Å, b= 102.59 Å, and c= 59.23 Å in an Amm2 (no. 38) symmetry group. Consistently, the most intense peak at 1.73° of our experimental PXRD matched with the peak corresponding to the (100) plane in the eclipsed pattern simulated from the COF model (Figure 2B). Moreover, Fourier-transform infrared spectroscopy (FT-IR) (Figures 2C and S1 of Supporting Information) showed the most important vibration peaks at 1621 and 1282 cm−1 (attributed to the CN and C−CN−C stretching of imine moieties), indicating the formation of the polyimine network. 10 In addition, the presence of phenanthroline fragments in this network was corroborated by the vibration found at 1603 cm−1, also observed in 1, which was attributed to the CN stretching. The vibration peak at 1697 cm−1was assigned to the CO stretching of unreacted aldehydes, which agrees with the appearance of Fermi resonance peaks at 2919 and 2850 cm−1. Moreover, the two peaks at 3349 and 3418 cm−1are related to the symmetric and asymmetric N−H stretchings of the free amino groups. The corresponding C−C aromatic ring stretchings at 1588, 1497, and 1432 cm−1and Caromatic−H stretchings centered at 3027 cm−1are also important in typical polyaromatic networks that contain TAPB as the building block. 10,12 In addition, solid-13C NMR experiments using Cross Polarization combined to Magic Angle Spinning (13C-CP-MAS) showed the characteristic iminic carbon peak at 156.4 ppm as well as the peaks centered at 153.2 and 150.1 ppm, which were assigned to the tertiary and quaternary carbons in the alpha position to the phenanthroline-nitrogen atom (Figure 2D. For the comparison with the 13C-CP-MAS spectrum of 1, see Figure S4 of Supporting Information). The rest of the signals correspond to several aromatic carbons present in the covalent structure. These results match with those observed in comparable pristine layered-COFs. 10 As indicated in Figure 2E, N2 sorption analysis at 77 K showed that Phen-COF is porous with a Brunauer−Emmett−Teller surface area (SBET) of 482 m2/g. The pore size distribution was calculated, finding pores of 13.4 and 15.6 Å (Figure S7 of Supporting Information). Finally, thermogravimetric analysis (TGA) showed that PhenCOF possesses good thermal stability, up to 300 °C even under an oxidant atmosphere (Figure 2F). In order to study the optical properties of Phen-COF, diffuse reflectance spectroscopy (DRS) was performed, revealing a continuous intense absorption of the material up to 450 nm (Figure S8 of Supporting Information). Applying Kubelka−Munk theory, the band gap of Phen-COF was found to be around 2.56 eV, which is comparable to that of other pristine layered imine-based COFs. 12 Additionally, fluorescence emission spectroscopy of Phen-COF showed broad emission bands with maximums centered at 470 and 537 nm, respectively (Figure S9 of Supporting Information). Electrochemical properties were determined by cyclic voltammetry measurements (Figure S10 of Supporting Information). One reduction and one oxidation process were observed at −0.10 and +0.82 V (vs Ag/AgCl), respectively. Reduction processes are expected due to the presence of phenanthroline, which is known as redox active at negative potentials (Figure S10, Supporting Information). The oxidation signal is attributed to the electron transfer from the valence band (VB) of the material, which leads to an energy value determined as 5.21 eV (see Figure 3 for determination of energy levels). 2.2. Postsynthetic Metalation. Postsynthetic metalation of Phen-COF consisted of dispersing it in acetonitrile and 6 M aqueous acetic acid in the presence of [(dF(CF3)ppy)2-Ir-μCl]2and NiCl2·glyme (see Supporting Information for further details). For this metalation, [(dF(CF3)ppy)2-Ir-μ-Cl]2was Figure 3. Energy levels of Phen-COF and Ir.Ni@Phen-COF. The values of the VB were calculated from the first oxidation signal of the cyclic voltammetry curve. Band gap values were obtained from the DRS spectra and subsequent application of Kubelka−Munk theory. ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12347 chosen as the iridium source 31 because it would enable the incorporation of a powerful photoredox complex through coordination with the phenanthroline ligands contained in Phen-COF. 6 NiCl2·glyme was selected as the Ni source due to the ability of glyme ligands to undergo exchange with phenanthroline moieties. Note that acetic acid was used in the metalation process because it was essential to preserve the crystallinity of Phen-COF, 32 as its absence always led to amorphization of the structure. The content of Ir and Ni incorporated into the metallated Phen-COF (hereafter called Ir,Ni@Phen-COF) was analyzed by total X-ray fluorescence (TXRF, see Supporting Information, Figure S17). 33 We found that the Ir and Ni contents in Ir,Ni@Phen-COF are 4.0 and 2.8% in weight, respectively. These values mean that 45% of the phenanthroline ligands present in Phen-COF coordinates to metals: 15% to Ir and 30% to Ni. Interestingly, the metal uptake from the solution is quite efficient. In fact, the 71% of the Ir species in solution is incorporated into the material, while the 82% of the Ni precursor is bound to the framework. Thus, the Ir/Ni ratio in the precursor’s solution is kept in the postfunctionalized material. Moreover, FT-IR, 13C NMR-CPMAS, PXRD, TGA, and FE-SEM performed on Ir,Ni@Phen-COF did not show any significant differences between the pristine and metallated Phen-COF (see Supporting Information). The energy-dispersive X-ray (SEM−EDX) mapping images showed the presence of homogeneously distributed C, N, Ir, Ni, Cl, and F atoms in the framework (see Figure S16 in Supporting Information). This result is in accordance with the X-ray photoelectron spectroscopy (XPS) analysis results of the bimetallated material (Figures S24 and S25 of Supporting Information). The binding energy of the Ni 2p band at 855.9 eV corresponds to Ni(II) species, which is close to that of the NiCl2(bpy) complex, 26,34 suggesting the coordination of Ni to the phenanthroline ligands present in the framework. The two peaks located at 62.2 (Ir 4f7/2) and 65.3 (Ir 4f5/2) eV are indicative of octahedral Ir(III) polypyridyl species coordinated tobothC,NandN,Nbidentateligands, 35,36 which is consistent with the proposed expected coordination of Ir complexes to the phenanthroline ligands of the framework, as can be seen in Figure 1. The peak at 688 eV is assigned to fluorine (F 1s) present in the ligands of the Ir complex. 35 Furthermore, the N 1s signal centered at 399.1 eV is similar to the observed features for related materials containing pyridyl and iminic nitrogen atoms reported in the literature. 37 Interestingly, the presence of Ir and Ni centers has a significant impact on the N 1s XPS features. While the signals observed in the pristine material are conserved, also electrons at lower energies are detected (Figure S26 of Supporting Information). According to previous reports, 37 pyridinic N atoms are observed at lower energies than the iminic ones. Therefore, this observation indicates that N-phenanthroline atoms are affected by the presence of metal centers. Thus, these data are consistent with the coordination of phenanthroline units to Ni and Ir fragments. Transmission electron microscopy (TEM) of Ir,Ni@PhenCOF confirmed the absence of inorganic nanoparticles (see Supporting Information, Figure S44, left). Ir,Ni@Phen-COF conserved the porosity with a SBET of 432 m2/g (see Supporting Information, Figure S17). The pore size distribution analysis showed values of 13.4 and 15.6 Å (Figure S18). With respect to the optical properties of Ir,Ni@Phen-COF, DRS unveiled a slight increase of the visible absorption of this material in comparison with the pristine one (Figure S20, Supporting Information). This observation is translated into a decrease in the band gap of the material, which changes from 2.56 eV in the pristine material to 2.29 eV in the metallated one. Moreover, the fluorescence emission spectra showed again a broad emission band at the same wavelengths than that observed for the pristine material. However, also a sharp emission at 442 nm becomes the maximum intensity signal in the spectrum (Figure S21). Furthermore, electrochemical features of the organic material mask the expected signals for the metal centers (Figure S22). As a consequence, no significant differences between pristine and metallated materials are observed by cyclic voltammetry, and the valence band value was determined to be −5.29 eV (see Figure 3). 38 Considering that only the bimetallated material is active in the catalytic process (see below), it is worth noting that properties determined by electrochemical measurements are not relevant for such activity. Theroleofphenanthrolinewasfurtherlyprovedby comparing the metal uptake of Phen-COF with that of a well-known layered imine-based COF without coordinating units. This imine-based COF has been previously studied in the incorporation of metal centers for catalysis, such as Pd(II). 12 These materials (Phen-COF and Crystalline Laminar-COF) were incubated under the same specific reaction conditions in the presence of Ir and Ni metal precursors. Remarkably, very low quantities of both metal centers were found after TXRF analyses (<0.1%), using the COF without phenanthroline fragments (see Supporting Information, Figure S40). It is worth noting that the procedure used in these essays includes an exhaustive overnight washing by Soxhlet extraction. This treatment can wash out molecular metallic species that could interact weakly with the COF structure as a result of supramolecular interactions 39 or through coordination to the iminic nitrogens. 40 Therefore, strong metal−phenanthroline interactions resulting from the chelating effect stabilizes the metalation of the COF structure, even after exhaustive washing. As a consequence, a robust heterogeneous catalytic system is achieved by using PhenCOF as a porous platform, in which the metallic sites will be permanently immobilized over the whole catalytic procedure. Additionally, this metalation process was repeated forming the mono-metallated Ni@Phen-COF and Ir@Phen-COF with a Ir and Ni loading of 3.9 and 2.9% in weight, respectively (see Supporting Information, Figures S31 and S37). Remarkably, these values are similar to those found for Ir,Ni@Phen-COF, making them good materials to be used as control in catalytic experiments for comparison purposes (vide infra). 2.3. Catalytic Activity. The catalytic performance of Ir,Ni@Phen-COF was initially evaluated studying as a model reaction the light-mediated cross-coupling between potassium benzyltrifluoroborate and 4-bromotoluene, which was reported using an homogeneous catalytic system by Molander and coworkers. 7 To our delight, bimetallated Ir,Ni@Phen-COF effectively catalyzed this reaction, reaching 90% conversion under blue light irradiation (Table 1, entry 1; see optimization in Table S2 of Supporting Information). As control experiments, we evaluated the performance of the pristine PhenCOF (Table 1, entry 2). In addition, we also carried out the reaction in the absence of any catalyst or under dark conditions (Table 1, entries 3 and 4). In the three cases, we observed negligible conversion. Moreover, the use of the PostFunctionalized-Crystalline Laminar-COF with an extremely ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12348 low content of Ni showed no conversion (Table 1, entry 5). In order to disclose the effect of having a heterogeneous system that included both Ni and Ir centers in the same material, we tried the reaction using the mono-metallated Ni@Phen-COF or Ir@Phen-COF, observing zero conversion in both cases (Table 1, entries 6 and 7). In the case of Ni@Phen-COF,itis worth mentioning that no product formation was observed, due to the lack of the photocatalytic unit. Therefore, the Ir center is required to generate the desired product. Nevertheless, when Ni@Phen-COF and Ir@Phen-COF were mixed in the same reaction medium, the photocatalytic process did not result in any product either (Table 1, entry 8). These observations are indicative of the requirements for the appropriate cooperativity in dual heterogeneous photocatalysis. In fact, these results account for a mechanism implying very reactive radical intermediates, which is characteristic of dual catalysis. Otherwise, in the reported molecular Ir/Ni dual catalysis in solution, their interplay depends on concentration and diffusion of active intermediates and catalysts. Thus, despite interesting activities have been reported in homogenous systems, the variable proximity in solution of catalytic sites can limits their efficiency. Design of heterobimetallic materials fixes the proximity between Ir and Ni centers, optimizing their cooperativity, which represents an advantage of the heterogeneous system with respect to the homogeneous one. To assess the advantage of the bimetallated COF versus a mixture of comparable homogeneous catalysts, we tested the performance of the molecular version of our catalytic system. To this end, we studied the reaction using as catalysts [Ir(dF(CF3)ppy)2(bpy)]PF6and [NiCl2(phen)] in the catalytic loadings analogous to the Ni and Ir contents in Ir,Ni@ Phen-COF (0.7 and 0.3 mol %, respectively). Remarkably, when the homogeneously catalyzed reaction was performed, the reaction reached 23% conversion (Table 1, entry 9), while almost full conversion was achieved using the bimetallated material under comparable conditions. This observation points out the limitation of the homogeneous system, which is probably due to the formation of unreactive aggregated Ni/ NiO particles. 9 Accordingly, after one catalytic run, it was observed that a dark solid is formed. Finally, we also studied the influence of metal-loading on the catalytic outcome. For this purpose, maintaining the 2:1 molar ratio between Ni and Table 1. Experiments for the Light-Mediated CrossCoupling between Potassium Benzyltrifluoroborates and Aryl Bromides a entry catalyst yield (%) b TON (Ir/Ni) 1Ir,Ni@Phen-COF (1.2 mg, 4.0% Ir, 2.8% Ni) 90 270/118 2Phen-COF (1.2 mg) 0 3 No Catalyst 0 4Ir,Ni@Phen-COF (1.2 mg) (dark) 0 5PF−Crystalline Laminar COF (1.2 mg) 0 6 Ni@Phen-COF (1.2 mg) 0 7 Ir@Phen-COF (1.2 mg) 0 8 Ni@Phen-COF (0.6 mg) Ir@Phen-COF (0.6 mg) 0 9 [Ir(dF(CF3)ppy)2(bpy)]PF6(0.3 mol %) [NiCl2(phen)] (0.7 mol %) 23 69/30 10 Ir,Ni@Phen-COF (1.2 mg, 7.0% Ir, 4.2% Ni) 87 149/76 11 Ir,Ni@Phen-COF (1.2 mg, 2.0% Ir, 1.4% Ni) 25 150/66 12 Ir,Ni@Phen-COF (1.2 mg, 2.2% Ir, 2.8% Ni) 42 229/55 13 Ir,Ni@Phen-COF (1.2 mg, 9.0% Ir, 2.8% Ni) 46 61/60 a The reaction was carried out using 2a (0.15 mmol), 3a (0.075 mmol), 2,6-lutidine (0.26 mmol), the corresponding catalyst, and 1 mL of solvent under an Ar atmosphere and blue light irradiation (blue LEDs, 23 W, 450 nm). b The yield was determined by 1H NMR using nitromethane as the internal standard. Scheme 2. Scope of Light-Mediated Cross-Coupling between Potassium Benzyltrifluoroborates and Aryl Bromides a a The heterogeneously catalyzed reaction (Het.) was performed using Ir,Ni@Phen-COF as the catalyst. The homogeneously catalyzed reaction (Homo.) was performed using [Ir(dF(CF3)ppy)2(bpy)]PF6and [NiCl2(phen)] as catalysts. The yields were determined by 1H NMR using nitromethane as the internal standard ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12349 Ir centers, we obtained two other different materials: one by doubling and the other by halving the amount of metal precursors employed in the postfunctionalization stage. Under the same conditions, both materials did not improve the yields observed for the initial Ir,Ni@Phen-COF (see Table 1, entries 10 and 11, and Table S3 of Supporting Information). The optimal Ni/Ir ratio found was 2:1 because other proportions (such as 4:1 and 1:1) gave worse yields and TONs (see Table 1, entries 12 and 13, and Table S3 of Supporting Information). The applicability of our heterogeneous system has been also evaluated for a variety of aryl bromides, allowing not only the introduction of several electron withdrawing or electron donating groups, but also more hindered or even with olefinic substituents. Thus, eight different unsymmetrical diarylmethanes were isolated from moderate to good yields applying this heterogeneous system. In all the studied cases, the observed catalytic activity for Ir,Ni@Phen-COF was, at least, double that the observed for the homogenously catalyzed version (Scheme 2). In order to further evaluate the scope of this dual heterogeneous catalytic system, we explored the use of other radical precursors of different nature. Therefore, we decided to substitute potassium benzyltrifluoroborate by tert-butoxytrifluoroborate, from which radical formation is thermodynamically slightly less favored. 41 Under the same reaction conditions, the photocatalytic cross-coupling between this substrate and 4-bromobenzonitrile was effectively performed, obtaining 76% of yield of product 6 (Table 2, entry 1). However, the homogeneously catalyzed reaction only achieved 12% of yield under the same reaction conditions (Table 2, entry 8). For this reaction, it was impossible to reach any conversion when the reaction was carried out in absence of a catalyst, or by the monometallic functionalized COFs, or when both monometallic materials were mixed in the same reaction medium (Table 2, entries 3 to 7). Another interesting type of reagents that can trigger photomediated cross-couplings are organic silicates. These substrates can offer some advantages in comparison with organic potassium trifluoroborates, such as avoiding byproducts, better solubility, and easier generation of unstabilized primary radicals because their redox potential is lower. 42 Therefore, we performed the light-mediated cross-coupling between organic silicate 7and 4-bromobenzonitrile under typical reaction conditions and using Ir,Ni@Phen-COF as a heterogeneous photocatalyst. As a result, the reaction reached 92% of yield after 14 h of irradiation at room temperature (Table 3, entry 1). Control experiments showed again that proximity and cooperativity between immobilized Ir and Ni complexes into Phen-COF were indispensable for triggering this organic transformation (Table 3, entries 2 to 7). In addition, the homogeneously catalyzed reaction only gave 26% under analogous conditions (Table 3, entry 8). Alternatively, proline derivatives can also be used as radical precursors. The photocatalytic decarboxylative arylation of alkyl carboxylic acids is interesting from the chemical point of view, because of the easy accessibility to these radical precursors and the potential interest of heterocyclic chemistry. 43 Thus, we performed the photocatalytic cross-coupling between N-protected proline 9and 4-bromobenzonitrile under reaction conditions previously reported for a homogeneous system (see Supporting Information for further details). 43 In this case, acetonitrile was employed as a solvent and cesium carbonate as a base to trigger the deprotonation of the corresponding α-amino acid derivative. In this case, the reaction catalyzed by Ir,Ni@Phen-COF reached 86% of isolated yield of the corresponding cross-coupled product 10 (Table 4, entry 1), while the homogeneous version was stalled at 58% (Table 4, entry 8). No background (Table 4, entries 2 and 3) or monometallic-catalyzed reactions (Table 4, entries 5 and 6) gave rise to the desired product, neither when both Table 2. Experiments for the Light-Mediated CrossCoupling between Potassium tert-Butyltrifluoroborate and Aryl Bromides a entry catalyst NMR yield (%) b 1Ir,Ni@Phen-COF (1.2 mg) 76 2Phen-COF (1.2 mg) 0 3 No Catalyst 0 4Ir,Ni@Phen-COF (1.2 mg) (dark) 0 5Ni@Phen-COF (1.2 mg) 0 6Ir@Phen-COF (1.2 mg) 0 7Ni@Phen-COF (0.6 mg) Ir@Phen-COF (0.6 mg) 0 8 [Ir(dF(CF3)ppy)2(bpy)]PF6(0.3 mol %) [NiCl2(phen)] (0.7 mol %) 12 a The reaction was carried out using 5(0.15 mmol), 3e (0.075 mmol), 2,6-lutidine (0.26 mmol), the corresponding catalyst, and 1 mL of solvent under an Ar atmosphere and blue light irradiation (blue LEDs, 450 nm). b The yield was determined by 1H NMR using nitromethane as the internal standard. Table 3. Control Experiments for the Light-Mediated CrossCoupling between Organic Silicates and Aryl Bromides a entry catalyst NMR yield (%) b 1Ir,Ni@Phen-COF (1.2 mg) 92 2Phen-COF (1.2 mg) 0 3 No Catalyst 0 4Ir,Ni@Phen-COF (1.2 mg) (dark) 0 5Ni@Phen-COF (1.2 mg) 0 6Ir@Phen-COF (1.2 mg) 0 7Ni@Phen-COF (0.6 mg) Ir@Phen-COF (0.6 mg) 0 8 [Ir(dF(CF3)ppy)2(bpy)]PF6(0.3 mol %) [NiCl2(phen)] (0.7 mol %) 26 a The reaction was carried out using 7(0.225 mmol), 3e (0.15 mmol), the corresponding catalyst, and 3 mL of solvent under an Ar atmosphere and blue light irradiation (blue LEDs, 450 nm). b The yield was determined by 1H NMR using nitromethane as the internal standard. ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12350 monometallic-functionalized COFs were reunited in the same reaction container (Table 4, entry 7). The main observation of this work is that a heterogeneous system has a significantly higher catalytic performance than the analogous homogeneous counterparts. From the data found in the literature, 7,41−43 it can be concluded that the homogeneous system used in this work shows comparable activities to the previously published systems (see Table S3, Supporting Information). Furthermore, our heterogeneous Ir,Ni@PhenCOF catalyst allowed achieving significantly higher TONs than any of the homogeneous catalytic versions. 2.4. Leaching Tests and Recyclability. An important requirement of heterogeneous functionalized materials consists of avoiding the leaching processes of molecular active fragments into the reaction solution. 44 This is important because one of the most interesting advantages of heterogeneous catalysis is the easy separation of the catalyst (by a simple filtration) preventing the release of any spurious species into the pure fractions of products. In our case, under the experimental conditions of the four studied reactions, we discarded leaching processes through filtration of the catalyst after one catalytic run and analysis of the supernatant by ICP measurements. Analytical data revealed that no metal species were found in the solution after simple filtration of the catalyst. In addition, when the filtered solution was used in the presence of additional amounts of the different starting materials, we found no reactivity at all, indicating that no catalytic species were leached into the reaction media. Moreover, to prove the recyclability of our catalyst, Ir,Ni@ Phen-COF was recovered by centrifugation, confirming the preservation of its chemical identity by FT-IR (Figure 4). Crystallinity was retrieved after simple solvothermal treatment of the material (Figure 4). In addition, TEM reveals that Table 4. Control Experiments for the Light-Mediated Decarboxylative Arylation of Alkyl Carboxylic Acids. a entry catalyst NMR yield (%) b 1Ir,Ni@Phen-COF (1.2 mg) 86 2Phen-COF (1.2 mg) 0 3 No Catalyst 0 4Ir,Ni@Phen-COF (1.2 mg) (dark) 0 5Ni@Phen-COF (1.2 mg) 0 6Ir@Phen-COF (1.2 mg) 0 7Ni@Phen-COF (0.6 mg) Ir@Phen-COF (0.6 mg) 0 8 [Ir(dF(CF3)ppy)2(bpy)]PF6(0.3 mol %) [NiCl2(phen)] (0.7 mol %) 58 a The reaction was carried out using 6(0.225 mmol), 3e (0.15 mmol), caesium carbonate (0.225 mmol), the corresponding catalyst, and 4 mL of solvent under an Ar atmosphere and blue light irradiation (blue LEDs, 450 nm). b The yield was determined by 1H NMR using nitromethane as the internal standard. Figure 4. Recycling of Ir,Ni@Phen-COF as a heterogeneous photocatalyst for light-mediated cross-coupling of potassium benzyltrifluoroborates and bromobenzene. ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12351 nanoparticles were not formed during the catalytic process (see Supporting Information, Figure S42). Moreover, this material can be used for eight consecutive catalytic cycles with minor loss of activity, generating 1 mmol (168 mg) of diphenylmethane 4b using 5 mg of Ir,Ni@Phen-COF overall (Figure 4). In terms of TON, this catalyst showed after the eight runs 925 TON for Ir and 424 TON for Ni, confirming its sturdiness and recyclability. Finally, as a proof for the scalability of this system, we performed this reaction at 5 mmol scale, maintaining the catalyst loading at 5 mg. A yield of 79% was reached after 96 h of irradiation, which implies 3800 TON for Ir and 1650 TON for Ni. 2.5. Mechanistic Considerations. The mechanism for dual catalytic systems closely related to this work has been previously considered using homogeneous species 7 and MOFs with similar coordinating units (Figure 5). 27 According to the available data, it is well established that Ir(III) species in the excited state is able to oxidize the radical precursor, which generates paramagnetic species that binds to a Ni(I) center through radical trapping. The corresponding Ni(II) center is reduced by the transient Ir(II) intermediate, regenerating the Ir photocatalyst and producing a Ni(I) species that can furtherly evolve through an oxidative addition by reaction with an aryl bromide. The final product is generated by a reductive elimination process. Combination of emission and cyclic voltammetry measurements performed for [Ir(dF(CF3)- ppy)2(bpy)]PF6indicates that this species has a reduction potential at an excited state of +1.32 V versus SCE (see Supporting Information, Figure S1). This potential demonstrates that oxidation of the radical precursors employed in this work (Eox from −0.87 to −1.11 V vs SCE) 7,41−43,45 is plausible. Furthermore, comparison of measured reduction potential of the [NiCl2(phen)] complex with the data obtained using [Ir(dF(CF3)ppy)2(bpy)]PF6indicates that Ir(II) + Ni(II) → Ir(III) + Ni(I) is thermodynamically feasible (see Supporting Information, Figure S1). Therefore, our data are fully consistent with the mechanistic scenario previously proposed for Ir/Ni dual catalytic systems. 3. CONCLUSIONS The predesign, synthesis, and characterization of a new phenanthroline-containing imine-based layered COF have been performed in this work. This new material was postfunctionalized with Ir and Ni metal complexes in order to obtain a heterogeneous photoredox nickel dual catalytic system. In this unprecedented COF, the phenanthroline group plays a key role in stabilizing the coordination of the metal centers. The obtained Ir,Ni@Phen-COF presents high catalytic activity toward photocatalytic cross-couplings between aryl bromides and four different radical precursors (NFigure 5. Mechanism of the transformations carried out in this work using Ir,Ni@Phen-COF as a heterogeneous dual catalytic system. ACS Catalysis pubs.acs.org/acscatalysis Research Article https://doi.org/10.1021/acscatal.1c03634 ACS Catal. 2021, 11, 12344−12354 12352