materials
Article
The Effects of Temperature Curing on the Strength
Development, Transport Properties, and Freeze-Thaw
Resistance of Blast Furnace Slag Cement Mortars
Modified with Nanosilica
Karol Federowicz 1, Vitoria Alves Figueiredo 2, Hussein Al-kroom 3,*,
Hamdy A. Abdel-Gawwad 4, Mohamed Abd Elrahman 5and Pawel Sikora 1,6,*
1Faculty of Civil and Environmental Engineering, West Pomeranian University of Technology Szczecin,
2Department of Civil Engineering, São Paulo State University (UNESP), Alameda Bahia, 550,
3Civil Engineering Department, The University of Jordan, Amman 11942, Jordan
4Raw Building Materials and Processing Technology Research Institute, Housing and Building National
Research Center (HBRC), 87 El-Tahreer St., Dokki, Giza, Cairo 12311, Egypt;
5Structural Engineering Department, Faculty of Engineering, Mansoura University, Elgomhouria St.,
6Building Materials and Construction Chemistry, Technische Universität Berlin, 13355 Berlin, Germany
*Correspondence: [email protected] (H.A.-k.); [email protected] (P.S.)
Received: 28 November 2020; Accepted: 15 December 2020; Published: 18 December 2020
Abstract:
This investigation studies the effects of hot water and hot air curing on the strength
development, transport properties, and freeze-thaw resistance of mortars incorporating low-heat
blast furnace slag cement and nanosilica (NS). Mortar samples were prepared and stored in ambient
conditions for 24 h. After demolding, mortar samples were subjected to two different hot curing
methods: Hot water and hot air curing (40
◦
C and 60
◦
C) for 24 h. For comparison purposes,
mortar reference mixes were prepared and cured in water and air at ambient conditions. Strength
development (from 1 to 180 days), capillary water porosity, water sorptivity, and freeze-thaw resistance
were tested after 180 days of curing. The experimental results showed that both curing regimes
accelerate the strength development of mortars, especially in the first seven days of hydration.
The highest early strengths were reported for mortars subjected to a temperature of 60
◦
C, followed
by those cured at 40
◦
C. The hot water curing regime was found to be more suitable, as a result of
more stable strength development. Similar findings were observed in regard to durability-related
properties. It is worth noting that thermal curing can more efficiently increase strength in the presence
of nanosilica, suggesting that NS is more effective in enhancing strength under thermal curing.
Keywords:
hot water curing; hot air curing; thermal curing; nanosilica; blast-furnace slag cement;
strength; freeze-thaw; sorptivity; porosity; cement mortar
1. Introduction
Dynamic developments in industry at a worldwide level poses new challenges for the construction
industry. The increase in the consumption of cement and concrete over the last decades, combined with
increased environmental awareness, has necessitated the use of new types of cements [
1
]. Binary or
ternary blended cement systems are increasingly being used to reduce carbon footprints [
2
]. One of the
most popular of these, blast-furnace slag cement (CEM III), can be distinguished according to EN 197-1.
Materials 2020,13, 5800; doi:10.3390/ma13245800 www.mdpi.com/journal/materials
Materials 2020,13, 5800 2 of 15
As has been shown numerous times in the existing literature, CEM III has a positive effect in improving
consistency and durability parameters. Moreover, thanks to its low hydration heat, it is more suitable
in mass structures [
3
–
7
]. Elements made of slag cement are also more resistant to chemical aggression,
such as that which is brought about by sulphates and chlorides [
8
]. Unfortunately, due to the presence
of slag glass phases, such composites suffer from low early strength and hardening [
8
]. Despite the
many advantages of concrete structures and their overall durability, exposure to harsh environments
containing chloride ions, carbon dioxide, or sulphate can reduce their durability and performance over
the years [
9
–
12
]. A generally accepted reason for why concrete is susceptible to chemical aggression is
that its porosity and microstructural defects allow harmful ions to penetrate the surface into the inside
of the concrete structure, ultimately resulting in cracks [
13
,
14
]. A common process of destruction
involves sulphate penetration through the surface, which then reacts with hydrates and produces
ettringite or gypsum, leading to volume expansion [
15
,
16
]. This creates tensile stresses in the concrete,
which result in subsequent cracks. Thus, it is very important to produce composites with dense and
compacted microstructures and satisfactory early mechanical performance.
Due to financial and technological reasons, high early strength is also demanded in the case
of prefabrication technology. Acceleration of the hydration process, and thus strength gain, can be
achieved by using the appropriate technical admixtures or special maturing techniques. There is
no single fixed procedure and thus various approaches are presented in the literature, including
steam curing, autoclaving, hot water curing, and hot air curing [
17
]. There is still no agreement as to
the proper curing method and no consensus as to which one best guarantees satisfactory composite
performance after curing. Some researchers suggest that the temperature curing process should take
place after the initial set and that the temperature should not exceed 60–70
◦
C [
18
,
19
], while other
researchers apply heating directly after casting [17].
The exposure of cementitious composites to elevated temperatures in the early ages causes internal
water loss by self-desiccation and it is thus of key importance to facilitate water/moisture from external
sources, during the heating process. Moreover, a thermally accelerated hydration process may result
in non-uniform scattering of the hydration products, consequently creating very high porosity and
cracking at later ages [
17
,
18
,
20
]. This phenomenon, often referred to as the crossover effect (COE),
may lead to a decrease in the mechanical performance of composites at later ages [
17
]. To tackle this
challenge, some authors have recommended that heating processes should not start directly after
casting, i.e., within 24 h of curing [
21
,
22
]. Studies by Mardani et al. [
23
] and Wang et al. [
24
] have
observed increases in compression strength during the first seven days, by using high temperature
curing 24 h after casting. However, their results do not agree on subsequent strength. Sajedi and
Razak [
25
] have reported that manipulating both the temperature and duration of heating enables
effective control of early strength development, as well making it possible to avoid the crossover effect.
Based on the available literature, it can be concluded that there is still no agreement on a
proper thermal curing method. Moreover, most of the available studies are solely related to the
strength development process, but this may be insufficient for establishing which curing technique
is the most effective. As has been proven by Zou et al. [
26
], it is necessary to supplement tests of
strength development processes with evaluations of durability-related properties, such as capillary
water absorption. The capillary water absorption (CWA) of concrete reflects not only changes in the
microstructure of the concrete surface, but is also indirectly related to its durability [
27
–
30
]. CWA
correlates well with the internal pores of concrete, as well as its water sorptivity. Both of these
parameters are often used to determine and compare the permeability of concrete [
31
–
33
]. Liu et al. [
31
]
have indicated that CWA also correlates well with the durability indicators of concrete.
Another approach for accelerating early strength development involves the incorporation of
nanoparticles; i.e., calcium-silicate-hydrate seeds (C-S-H) or nanosilica (NS). It has been widely
recognized that the use of nanosilica has a substantial effect on the acceleration of the cement hydration
process, thus leading to faster setting and hardening of cementitious composites [
34
–
36
]. The beneficial
effects of nanosilica on the properties of cementitious composites, in fresh and hardened states, can be
Materials 2020,13, 5800 3 of 15
attributed to three synergistic NS effects: Nucleating, filling, and high pozzolanic activity [
37
–
39
]. The
effects of NS on the cement hydration process of Ordinary Portland Cement (OPC) and on binary
cementitious systems under ambient [
40
,
41
] and elevated temperatures [
42
,
43
] have been confirmed
by calorimetric studies.
As far as the authors of this work are aware, research on the mechanical and durability performance
of thermallycured binarycementitious systems, modifiedwith silica nanoparticles, hasbeen limited[
44
].
There is therefore a strong need to explore the effects of temperature curing on the long-term
durability-related properties of cementitious composites. In addition, for precast concrete such
technology is imperative in order to improve the efficiency and the characteristics of the precast
elements for such aggressive conditions. This study aims to fill the gap in the existing knowledge and
to shed light on the effects of temperature curing on the strength development, transport properties,
and freeze-thaw resistance of low-heat blast-furnace slag cement mortars modified with nanosilica.
Two different curing methods (hot air and hot water) and two heating temperatures (40
◦
C and 60
◦
C)
were evaluated and compared with control specimens cured in ambient conditions (20 ◦C).
2. Materials and Methods
2.1. Materials
In this investigation, low heat blast-furnace slag cement CEM III/A 42.5 N—LH/HSR/NA, produced
by G
ó
ra˙zd˙ze (Chorula, Poland), river sand with particle sizes up to 2 mm (Bielinek, Poland), and
tap water were used. Moreover, a silica colloidal suspension with a solid mass of 50 wt.-% was
used. The general properties of the nanosilica (NS) are presented in Table 1. Figure 1a,b confirms the
spherical shape of the silica nanoparticles, with X-ray diffraction confirming its high purity (Figure 1d).
According to transmission electron microscopy (TEM) micrographs, NS particle sizes ranged 10–140 nm
(Figure 1c). Detailed information regarding the nanosilica used in this study can be found in our
previous work [40]. The particle size distribution (PSD) of the cement used in this study is presented
in Figure 2. It can be clearly seen that NS was much finer than the particle size of the cement.
Table 1. Properties of colloidal silica.
Particle Size Solid Content Density Viscosity pH
10–140 nm * 50 wt.-% 1.4 g/cm38 cP 9.5
* based on TEM analysis.
Figure 1. Cont.
Materials 2020,13, 5800 4 of 15
Figure 1.
TEM images (
a
,
b
), size distribution (
c
), XRD (
d
) of nanosilica (NS). Reproduced from
Sikora et al. 2020 [40].
Figure 2.
Particle size distribution of cement and river sand used in this study. The particle size range
(based on TEM analysis) of silica nanoparticles has been highlighted in yellow.
2.2. Mixture Design and Mixing Process
The mortar component proportions and the mixing procedure conformed to EN 196-1. The mortars
were produced with a cement: River sand fixed ratio of 1:3. The w/c was fixed at 0.5. Reference mixtures
(without nanosilica) were designated as series C, while mixtures containing nanosilica were designated
as series N. Nanosilica suspension was mixed with water, prior to mixing with dry components. Based
on our previous studies [
40
,
41
,
45
], 3% of nanosilica (by mass of cement) is the most effective dosage
and it was therefore incorporated in the mortars. After mixing, the mortar samples were molded in
40
×
40
×
160 mm
3
prisms for water accessible porosity and water sorptivity tests, while 40
×
40
×
40 mm
3
cubical specimens were produced for compressive strength and freeze-thaw resistance tests.
After 24 h of storing in ambient conditions, the specimens were demolded and subjected to various
curing processes, which have been presented in the next section. In total, 72 prismatic and 576 cubic
specimens were produced in this study.
2.3. Experimental Protocol
After 24 h of casting, the specimens were demolded and assigned to different curing conditions.
In the research presented here, all samples were named according to a scheme in which the first
letter designated whether it was a control (C) mix or a mix with nanosilica (N); the following number
Materials 2020,13, 5800 5 of 15
corresponded to the temperature at which a sample was cured, for between 24 h and 48 h (20/40/60);
the last letter designated the type of curing (A—on air, W—in water). For instance, N40W refers to
nanosilica-modified cement mortar cured for 24 h in water, at 40
◦
C. Series C40A, N40A, C60A, and
N60A were wrapped in foil and exposed to air-oven curing for 24 h hours, at temperatures of 40
◦
C
and 60
◦
C. Series C40W, N40W, C60W, and N60W were put in a sealed water tank and exposed to
hot water curing for 24 h hours, at temperatures of 40
◦
C and 60
◦
C. After the heating procedures,
the specimens were stored in water for up to 28 days of curing. Two series of mortars were prepared as
control specimens. After demolding, mortars C20A and N20A were wrapped in foil and stored at a
temperature of 20
◦
C
±
2
◦
C and RH =65
±
5%, for up to 28 days. Mortars C20W and N20W were
stored in a water tank at a temperature of 20
◦
C
±
2
◦
C, for up to 28 days. After 28 days, the specimens
were removed and cured for up to 180 days at ambient conditions (20
◦
C
±
2
◦
C and RH =65
±
5%).
A detailed experimental protocol is presented in Figure 3.
Figure 3. Experimental curing method protocol.
2.4. Method
2.4.1. Compressive Strength
The compressive strength of the mortars was determined with a digital crushing machine (Toni
Technik -Zwick-Roell, Berlin, Germany), conforming to EN 196-1. Six cubes of each type of mortar mix
were tested, with the mean value taken into consideration. After the planned curing period and at a
specific age, the surfaces of the specimens were dried and the test was carried out.
2.4.2. Capillary Water Porosity
The capillary water porosity of 40
×
40
×
160 mm
3
mortar prisms was determined using the water
displacement method, based on the Archimedes principle [
46
]. After 180 days of curing, the mass of
saturated samples was measured under water (m
sub
). Afterwards, the surfaces of the specimens were
dried and the mass of the saturated sample was determined (m
sat
). Finally, the specimens were dried
at 105
◦
C to a constant mass and weighed (m
dry
), with the capillary water porosity calculated using the
following formula (Equation (1)):
Capillary water porosity [%]=msat −mdry
msat −msub
×100 (1)
Materials 2020,13, 5800 6 of 15
where, m
sat
, the mass of saturated sample, m
dry
is mass of the dry sample, and m
sub
is the underwater
mass of the submerged sample.
2.4.3. Water Sorptivity
The water absorption coefficient of the mortars was calculated based on the water sorptivity test,
using the partial immersion method according to the guidelines of EN ISO 15148. Prior to the test,
the sides of three 40
×
40
×
160 mm
3
prisms of each type of mortar were sealed with hot paraffin wax.
During measurement, the water level was kept constant at about 5 mm above the highest point of
the bottom side of the prism (Figure 4). A detailed explanation of the procedure can be found in our
previous work [46].
Figure 4.
Schematic set-up for measuring the rate of water absorption in cement mortar specimens.
Reproduced from [46].
2.4.4. Freezing and Thawing Resistance
Freeze-thaw resistance was determined according to the Polish Standard PN-85-B-04500 [
47
]
(Figure 5). Firstly, 40
×
40
×
40 mm
3
cubic specimens were used to determine the compressive
strength of the mortars after the freezing and thawing test. After 180 days of curing, specimens were
oven-dried at 105
◦
C, until constant mass, and once again saturated in water for 7 days, after which
they were exposed to 25 freeze-thaw cycles (group T25). The group T0 samples remained in water,
at a temperature of 20
◦
C, without exposure to freezing and thawing. Basic freeze-thaw resistance
was determined after 25 cycles, with each cycle lasting 8 h, during which the samples were frozen
for 4 h in air at
−
20
◦
C and then thawed for another 4h in water at 20
◦
C. For each mix design, a total
of 12 specimens were used; six specimens for group T0 and six for group T25 (25 cycles). In total,
144 specimens were tested with the freeze-thaw procedure.
Figure 5. Freezing and thawing cycle.
Materials 2020,13, 5800 7 of 15
2.4.5. Mercury Intrusion Porosimetry
Mercury intrusion porosimetry (MIP) was applied in order to assess the pore characteristics of the
cement mortars. This is a common method widely used to characterize the pore structure of porous
materials, including the cement-based and geopolymer composites used in construction [
48
,
49
]. Due to
its simplicity, quickness, and wide pore diameter measuring range, it can be used as an indicator for
understanding the durability related parameters of composites, including transport properties and
freeze-thaw resistance [
49
]. MIP tests were performed on small-cored mortar samples taken out from
the middle of the specimens. Prior to measurement, the samples were placed in a freeze dryer to stop
hydration and remove pore moisture.
3. Results
3.1. Compressive Strength Development
Figure 6presents the experimental results of the compressive strength development of cement
mortars at up to 180 days of curing. In general, a similar strength development trend can be seen with
both techniques, for up to 28 days of curing, with curing temperature having a major influence. At an
age of one day (after demolding), no differences between the compressive strength of the plain and
NS-modified specimens were reported. However, from two days of curing on, a difference between
the compressive strengths was observed, in favor of the N series. This effect can be attributed to the
pozzolanic activity of nanosilica, which results in consumption of Ca(OH)
2
and the production of
additional C-S-H phase [
40
,
50
]. In regard to temperature, it can be clearly seen that the proposed curing
methods have a significant effect on the early strength development of mortars. A temperature of 60
◦
C
had the highest impact on early strength values, followed by a temperature of 40
◦
C. After temperature
curing (two days), specimens C40A, N40A, C60A, and N60A exhibited 54%, 75%, 116%, and 139%
higher strengths than the C20A specimen. Similarly, specimens C40W, N40W, C60W, and N60W
exhibited 59%, 81%, 121%, and 137% higher compressive strengths than the C20W specimen.
Figure 6.
Specimens’ compressive strength development for up to 180 days of hot air curing (
a
) and
hot water curing (b).
The incorporation of NS to the mixture was beneficial in the improvement of the compressive
strength of specimens, with NS-modified specimens exhibiting higher compressive strengths than the
corresponding control mortars; the effect was more pronounced in specimens that were thermally
cured. The increase in the strength with nanosilica addition is in the range of 5–20% depending on
the mortar age as well as the applied curing regime. This observation is in line with Mei et al.’s [
44
]
study, where it was found that a combination of nanosilica and temperature curing promotes cement
hydration. In general, the discrepancy between the compressive strength values attributed to thermal
curing are visible for up to 14 days of curing. Afterwards, considerable differences between specimens
Materials 2020,13, 5800 8 of 15
were not observed. After 28 days of curing, specimens containing NS exhibited only a slight strength
improvement; on average by 8%. A review of the literature shows that NS exhibits noticeable effects,
both on early and later strength development, although most studies have focused on OPC systems.
However, in our case, low heat blast-furnace slag cement was used and thus the reaction rate of NS
and cement was most probably slightly lower than in a pure OPC system. Moreover, irrespective of the
curing method used, mortars exhibited only a minimal strength decrement, not exceeding 8%. It was
thus confirmed that, when thermal curing is applied after 24 h of hydration, rather than directly after
casting, the crossover effect is limited.
Figure 7presents strength development in days (age). It can be clearly seen that the heating
process (2 days) made a major contribution to the 28 days compressive strength. The effect was more
pronounced with an increment in temperature and it can be seen that hot air curing made a higher
contribution to 28 days strength, than the water curing method. Nevertheless, despite noticeably higher
acceleration of strength development, compressive strength development in hot air cured specimens in
later ages was impeded, in favor of the hot water cured specimens. This was especially visible at 14
days, where all hot water cured specimens almost reached the 28 days strength, while specimens C60A
and N60A reached less than 90% of 28 days of compressive strength. Incorporation of nanosilica in the
mixture was found to have a beneficial effect on accelerating the strength gain of specimens in ambient
conditions, as well as during exposure to a temperature of 40 ◦C.
Figure 7. Development of strength of hot air-cured (left) and hot water-cured specimens (right).
To determine the possibility of the presence of the crossover effect, the compressive strengths of
mortar specimens were additionally measured after 180 days of curing (Figure 6). After 180 days of
curing, the choice of curing method seems to have a much more pronounced effect on the compressive
strength, than at 28 days. This can be attributed to fact that low heat blast-furnace slag cement was
used, which is widely known to have a relatively slow hydration process. In the case of the hot air
curing method, it can be seen that specimens C20A and N20A exhibited the lowest strengths in this
group. This can be attributed to the fact that, after demolding, specimens were cured in air conditions
and thus a limited amount of moisture was available for hydration. On the contrary, specimens C40A,
N40A, C60A, and N60A, after air curing process, were stored underwater until 28 days of age (Figure 3).
In the case of hot air cured specimens, the best performance was achieved by specimens exposed to a
temperature of 40
◦
C (C40A and N40A), followed by those exposed to a temperature of 60
◦
C. Despite
the noticeable effects of nanosilica in the early days of hydration, its effect on the compressive strength
of the specimens after 180 days was negligible.
Inthe caseofthewater-curedspecimens, allmortars besidesC60WandC20Wexhibited comparable
strengths, with the highest value reported for N20W. The compressive strength values of N20W, C40W,
N40W, and N60W were comparable to those of specimens that exhibited the best performance under
Materials 2020,13, 5800 9 of 15
hot air curing; namely, C40A and N40A. Similar to the case of the air curing method, mortars with and
without NS exposed to hot water curing exhibited comparable strength values. In contrast, the control
specimens, C20W and N20W, exhibited a discrepancy in their results, in favor of the NS-modified
specimen, which exhibited 16% higher strength.
Based on the compressive strength results, it can be concluded that the hot water curing method
facilitates more uniform strength development than oven-air curing. In addition, both temperatures of
40
◦
C and 60
◦
C seem to be suitable for enhancing the early strength development of low-heat cement
mortars. Furthermore, in both curing procedures, nanosilica is beneficial in accelerating strength
development, but at 28 days and 180 days, the beneficial effect of nanosilica is negligible.
3.2. Transport Properties
Figure 8presents the results of tests of capillary water porosity and the water absorption coefficient
of mortar specimens after 180 days of curing. In general, it can be seen that thermal curing had beneficial
effects on reducing the mortars’ transport properties. However, the hot air cured specimens exhibited
slightly worse transport properties than the water cured ones. In addition, significant improvements
were found for specimens containing nanosilica. Both the results of capillary water porosity and water
absorption showed a similar trend. After exposure to a temperature of 60
◦
C, the difference between
the NS-modified and control specimens was limited, confirming that a major influence on modification
properties is temperature exposure. Higher discrepancies can be discerned for air-cured specimens,
while lower ones were seen in the case of hot water cured specimens. The absorption coefficients of
water cured samples were lower than that of air cured ones. This influence was less pronounced for
capillary water porosity. It can also be clearly seen that the water absorption coefficient decreased with
capillary porosity. Additionally, the water absorption coefficient decreased with increasing curing
temperature, in both the hot air and hot water cases. For both properties it is clear that incorporation of
nanosilica has an influence in reducing the capillary porosity as well as the water absorption coefficient
in both cases: Air curing and water curing. In most mixes, direct relation between capillary porosity
and transport properties can be caught. However, for some mixes N20W and C40W, the absorption
coefficient is increasing with reducing the capillary porosity in the first and vice versa in the second
mix. This might be attributed to the differences in the pore structures, which cannot be measured by
the water sorptivity test.
Figure 8. Transport properties of cement mortars after 180 days of curing.
Materials 2020,13, 5800 10 of 15
3.3. Freezing and Thawing Resistance
The influence of freezing and thawing on the compressive strength of mortars, after 180 days of
curing, is presented in Figure 9. It is clear that, for the first series with hot air curing, as the curing
temperature increased, the strength deterioration after exposure to freezing and thawing increased
gradually. The control mix for the first series (C20A) lost about 40% of its original strength, due to
exposure to freezing and thawing cycles. However, by increasing the curing temperature to 60
◦
C,
strength loss increased to about 48% (C60A). The inclusion of NS had a marginal influence on strength
loss after exposure to freezing and thawing in air-cured specimens. In contrast, a different trend
was observed in water-cured specimens. The incorporation of nanosilica appeared to improve the
resistance of mortars, subjected to water curing, to freezing, and thawing. This observation is in line
with the available literature [
51
,
52
]. A large difference between C40W and N40W was not reported,
but these specimens exhibited substantially improved freezing and thawing resistance, as compared
to the C20W specimen. On the other hand, increasing the curing temperature to 60
◦
C resulted in a
slight decrement in residual strength, after exposure to freezing and thawing (C60W), although this
was partially suppressed by the presence of NS (N60W). It can also be seen that, in both groups, as
the curing temperature increased, the residual strength, after the freezing and thawing cycles, was
significantly reduced. This can be attributed to the influence of high temperature curing in accelerating
the hydration of the cement component randomly. The hydration products thus formed are weaker
than the ones formed without heat curing. However, the hydration degree of cement is higher, which is
reflected in compressive strength results before the test. When the samples were exposed to freezing
and thawing cycles, fast deterioration occurred in all of them, but it was more pronounced in samples
cured at high temperatures, due to the weakness of the C-S-H phases formed. The role of nanosilica
in reducing strength deterioration, after exposure to freezing and thawing, is more detectable in the
group of hot water cured specimens, as can be seen in Figure 9.
Figure 9. Compressive strength of mortar specimens, after exposure to freeze–thaw cycles.
3.4. Mercury Intrusion Porosimetry (MIP)
Figure 10 and Table 2present the results of MIP tests, after 180 days of curing. In general,
water curing was more efficient than air curing in all the mixes. In addition, the incorporation of
nanosilica reduced the porosity of most mixes, compared to the reference mixes. Regarding the
curing methods, it is clear that for most mixes, the total porosity decreased with increasing heating
temperature. For example, the porosity of C20A decreased from 13.05% to 10.35%, when cured with
hot air at a temperature of 40
◦
C (C40A). Similarly, for the hot water curing group, porosity decreased
Materials 2020,13, 5800 11 of 15
from 12.24% (C20W) to 10.67% at 40
◦
C; the only exception being mix C60W, where the porosity
increased with increasing curing temperature. However, noticeable differences in the average and
median pore diameters, between specimens, can be distinguished (Table 2). Specimens C20A and
N20A exhibited significantly higher porosities, due to the fact that they were directly air-cured after
demolding; limited moisture was thus available during the hydration process. Important differences
in the curve characteristics can be distinguished (Figure 10): The curves of the NS-modified specimens
shifted noticeably to a region of smaller pores, which confirms that the incorporation of NS has
substantial effects on pore structure alteration. This was reflected in the decrement of the average
and median pore values in the NS-modified specimens (Table 2). This study therefore confirms the
observations of other researchers [
53
], that the incorporation of NS in a mixture does not necessarily
have to have an impact on the decrement in cement matrix porosity, but that it has substantial effects
on pore structure alteration. As has been reported by other researchers, the presence of nanosilica in
cementitious composites results in the disconnection of continuous pores from discontinuous ones,
the subdivision of larger pores into smaller ones, as well as in the modification of the their shapes and
tortuosity [
54
,
55
]. This could explain the substantial improvement of transport properties in mortars
containing nanosilica (Figure 8). Nevertheless, the correlation between the results of MIP and freezing
and thawing resistance cannot be established directly.
Figure 10.
Cumulative intruded pore volume versus pore diameter of hot air-cured (
left
) and hot
water-cured specimens (right).
Table 2.
Porosities, average pore diameter, and median diameter of the cement mortars after 180 days
of curing.
Mix C20A N20A C40A N40A C60A N60A C20W N20W C40W N40W C60W N60W
Total intruded vol. [mm3/g] 61.60 70.83 48.77 43.94 50.21 59.56 61.75 55.06 52.47 62.25 71.09 48.69
Porosity by Hg intrusion [%] 13.05 13.78 10.35 9.38 10.03 12.22 12.24 11.12 10.67 12.75 13.46 9.86
Average pore diameter [nm] 51.61 62.52 26.28 25.46 25.94 25.82 28.61 22.58 29.96 27.8 25.45 26.41
Median pore diameter [nm]
256.12
216.3 40.46 34.66 36.47 25.1 49.84 28.46 49.01 52.96 32.8 38.53
4. Conclusions
The following conclusions can be drawn from this work:
•
The proposed curing methods have a considerable effect on the early strength development of
low heat blast-furnace slag cement mortars. A strength development trend, comparable to 28-day
curing, was noticed when both curing techniques were applied, with curing temperature having
a major influence. A temperature of 60
◦
C had the highest impact on the early strength values,
followed by a temperature of 40 ◦C.
•
Based on the compressive strength results, it can be concluded that the hot water curing method
facilitatesmoreuniformstrength developmentthanoven-air curing. In addition, bothtemperatures
(40
◦
C and 60
◦
C) were found to be suitable for enhancing the early strength development of low
Materials 2020,13, 5800 12 of 15
heat cement mortars. Moreover, irrespective on the curing method, mortars exhibited minimal
strength decrement. Thus, it was confirmed that, when thermal curing is applied after 24 h of
hydration and not directly after casting, the crossover effect is limited.
•
The incorporation of nanosilica in mixtures was found to have a beneficial effect in accelerating
specimens’ strength gain in ambient conditions, as well as during exposure to a temperature of
40
◦
C. However, at a temperature of 60
◦
C, the beneficial effects were limited, with the major
contribution being temperature. NS-modified specimens exhibited higher strength gains, after
thermal curing, than corresponding control (pristine) specimens.
•
Due to a substantially accelerated cement hydration process and thus early strength gain associated
with the synergistic effects of nanosilica and temperature, the effect of nanosilica on compressive
strength at 28 days and 180 days was found to be negligible.
•
Thermal curing had beneficial effects on improving the transport properties of mortars. The hot
air cured specimens exhibited slightly worse transport properties than hot water cured specimens.
In addition, significant improvements were reported in specimens containing nanosilica. MIP
studies confirmed that NS has substantial effects on refinement of the pore structure in a
cement matrix.
•
A slight decrement in the freezing and thawing resistance of thermally cured specimens was
found, but these changes did not exceed 10%. The incorporation of NS improved the resistance of
mortars subjected to water curing, to freezing, and thawing.
Author Contributions:
Conceptualization, P.S. and K.F.; methodology, K.F., P.S. and M.A.E.; software, K.F.;
validation, K.F., V.A.F. and P.S.; formal analysis, K.F., V.A.F., P.S. and M.A.E.; investigation, V.A.F., K.F., H.A.-k.
and H.A.A.-G.; resources, K.F. and P.S.; data curation, K.F. and P.S.; writing—original draft preparation, K.F.,
V.A.F., H.A.-k., H.A.A.-G., M.A.E. and P.S.; writing—review and editing, K.F., V.A.F., H.A.-k., H.A.A.-G., M.A.E.
and P.S.; visualization, P.S. and K.F.; supervision, K.F. and P.S.; project administration, P.S.; funding acquisition, P.S.
and H.A.-k. All authors have read and agreed to the published version of the manuscript.
Funding:
This project received funding from the European Union’s Horizon 2020 research and innovation
program, under the Marie Skłodowska-Curie grant agreement No. 841592.
Acknowledgments:
The authors express their sincere gratitude for the financial support provided by the Deanship
of The Scientific Research University of Jordan.
Conflicts of Interest: The authors declare no conflict of interest.
References
1.
Monahan, J.; Powell, J. An embodied carbon and energy analysis of modern methods of construction in
housing: A case study using a lifecycle assessment framework. Energy Build. 2011,43, 179–188. [CrossRef]
2.
Erdem, T.K.; Kırca, Ö. Use of binary and ternary blends in high strength concrete. Constr. Build. Mater.
2008
,
22, 1477–1483. [CrossRef]
3.
Tazawa, E.-I.; Miyazawa, S.; Kasai, T. Chemical shrinkage and autogenous shrinkage of hydrating cement
paste. Cem. Concr. Res. 1995,25, 288–292. [CrossRef]
4.
Darquennes, A.; Staquet, S.; Espion, B. Behaviour of slag cement concrete under restraint conditions. Eur. J.
Environ. Civ. Eng. 2011,15, 787–798. [CrossRef]
5.
Monkman, S.; Shao, Y. Carbonation Curing of Slag-Cement Concrete for Binding CO
2
and Improving
Performance. J. Mater. Civ. Eng. 2010,22, 296–304. [CrossRef]
6.
Divsholi, B.S.; Lim, T.Y.D.; Teng, S. Durability Properties and Microstructure of Ground Granulated Blast
Furnace Slag Cement Concrete. Int. J. Concr. Struct. Mater. 2014,8, 157–164. [CrossRef]
7.
Darquennes, A.; Staquet, S.; Delplancke-Ogletree, M.-P.; Espion, B. Effect of autogenous deformation on the
cracking risk of slag cement concretes. Cem. Concr. Compos. 2011,33, 368–379. [CrossRef]
8.
Schuldyakov, K.; Kramar, L.; Trofimov, B. The Properties of Slag Cement and its Influence on the Structure of
the Hardened Cement Paste. Procedia Eng. 2016,150, 1433–1439. [CrossRef]
9.
Su, Y.; Wei, X.; Huang, J.; Wang, Y.; He, X.; Wang, X.; Ma, B. Use of different barium salts to inhibit the
thaumasite form of sulfate attack in cement-based materials. J. Wuhan Univ. Technol. Sci. Ed.
2016
,31,
361–366. [CrossRef]
Materials 2020,13, 5800 13 of 15
10.
Jiang, W.; Li, X.; Lv, Y.; Zhou, M.; Liu, Z.; Ren, Z.; Yu, Z. Cement-Based Materials Containing Graphene
Oxide and Polyvinyl Alcohol Fiber: Mechanical Properties, Durability, and Microstructure. Nanomaterials
2018,8, 638. [CrossRef]
11.
Zhang, P.; Wittmann, F.H.; Lura, P.; Müller, H.S.; Han, S.; Zhao, T. Application of neutron imaging to
investigate fundamental aspects of durability of cement-based materials: A review. Cem. Concr. Res.
2018
,
108, 152–166. [CrossRef]
12.
Zuquan, J.; Wei, S.; Yunsheng, Z.; Jinyang, J.; Jianzhong, L. Interaction between sulfate and chloride solution
attack of concretes with and without fly ash. Cem. Concr. Res. 2007,37, 1223–1232. [CrossRef]
13.
Uthaman, S.; Vishwakarma, V.; George, R.; Ramachandran, D.; Kumari, K.; Preetha, R.; Premila, M.;
Rajaraman, R.; Mudali, U.K.; Amarendra, G. Enhancement of strength and durability of fly ash concrete
in seawater environments: Synergistic effect of nanoparticles. Constr. Build. Mater.
2018
,187, 448–459.
[CrossRef]
14.
Shaikh, F.U.A.; Supit, S.W. Chloride induced corrosion durability of high volume fly ash concretes containing
nano particles. Constr. Build. Mater. 2015,99, 208–225. [CrossRef]
15.
Ragoug, R.; Metalssi, O.O.; Barberon, F.; Torrenti, J.-M.; Roussel, N.; Divet, L.; De Lacaillerie, J.D. Durability of
cement pastes exposed to external sulfate attack and leaching: Physical and chemical aspects. Cem. Concr. Res.
2019,116, 134–145. [CrossRef]
16.
Deng, Y.; Zhang, C.; Wei, X. Influence of lithium sulfate addition on the properties of Portland cement paste.
Constr. Build. Mater. 2014,50, 457–462. [CrossRef]
17.
Sumra, Y.; Shafigh, P.; Ibrahim, Z.; Hashim, H.; Panjehpour, M. Crossover Effect in Cement-Based Materials:
A Review. Appl. Sci. 2019,9, 2776. [CrossRef]
18.
Liu, B.; Shi, J.; Zhou, F.; Shen, S.; Ding, Y.; Qin, J. Effects of steam curing regimes on the capillary water
absorption of concrete: Prediction using multivariable regression models. Constr. Build. Mater.
2020
,256,
119426. [CrossRef]
19.
Ezziane, K.; Bougara, A.; Kadri, A.; Khelafi, H.; Kadri, E. Compressive strength of mortar containing natural
pozzolan under various curing temperature. Cem. Concr. Compos. 2007,29, 587–593. [CrossRef]
20.
Lothenbach, B.; Winnefeld, F.; Alder, C.; Wieland, E.; Lunk, P. Effect of temperature on the pore solution,
microstructure and hydration products of Portland cement pastes. Cem. Concr. Res.
2007
,37, 483–491.
[CrossRef]
21.
Mardani-Aghabaglou, A.; Bursa Uludag University; Özen, S.; Altun, M.G.; Bursa Technical University.
Effect of curing conditions during the first 24 hours after casting on the properties of mortar mixtures.
Revista de la construcción2020,19, 68–79. [CrossRef]
22.
Jiang, C.; Jin, C.; Wang, Y.; Yan, S.; Chen, D. Effect of heat curing treatment on the drying shrinkage behavior
and microstructure characteristics of mortar incorporating different content ground granulated blast-furnace
slag. Constr. Build. Mater. 2018,186, 379–387. [CrossRef]
23.
Mardani, A.; Özen, S.; Altun, M.G.; Faqiri, Z.A. Effect of Water Curing Temperature on Compressive Strength
Development and Water Absorption Capacity of Mortar Mixtures. Sigma J. Eng. Nat. Sci.
2020
,38, 135–148.
24.
Wang, M.; Hu, Y.; Wang, Q.; Tian, H.; Liu, D. A study on strength characteristics of concrete under variable
temperature curing conditions in ultra-high geothermal tunnels. Constr. Build. Mater.
2019
,229, 116989.
[CrossRef]
25.
Sajedi, F.; A Razak, H. Thermal activation of ordinary Portland cement–slag mortars. Mater. Des.
2010
,31,
4522–4527. [CrossRef]
26.
Zou, C.; Long, G.; Ma, C.; Xie, Y. Effect of subsequent curing on surface permeability and compressive
strength of steam-cured concrete. Constr. Build. Mater. 2018,188, 424–432. [CrossRef]
27.
Tasdemir, C. Combined effects of mineral admixtures and curing conditions on the sorptivity coefficient of
concrete. Cem. Concr. Res. 2003,33, 1637–1642. [CrossRef]
28.
Liu, B.; Qin, J.; Sun, M. Influence of Silane-based Impregnation Agent on the Permeability of Concretes.
KSCE J. Civ. Eng. 2019,23, 3443–3450. [CrossRef]
29.
Kumar, S.; Kothiyal, A.D.; Bisht, M.S.; Kumar, A. Effect of nanofluid flow and protrusion ribs on performance
in square channels: An experimental investigation. J. Enhanc. Heat Transf. 2019,26, 75–100. [CrossRef]
30.
Shi, J.; Liu, B.; Qin, J.; Jiang, J.; Wu, X.; Tan, J. Experimental study of performance of repair mortar: Evaluation
of in-situ tests and correlation analysis. J. Build. Eng. 2020,31, 101325. [CrossRef]
Materials 2020,13, 5800 14 of 15
31.
Liu, B.; Luo, G.; Xie, Y. Effect of curing conditions on the permeability of concrete with high volume mineral
admixtures. Constr. Build. Mater. 2018,167, 359–371. [CrossRef]
32.
Yu, Z.; Ni, C.; Tang, M.; Shen, X. Relationship between water permeability and pore structure of Portland
cement paste blended with fly ash. Constr. Build. Mater. 2018,175, 458–466. [CrossRef]
33.
De Schutter, G. Evaluation of water absorption of concrete as a measure for resistance against carbonation
and chloride migration. Mater. Struct. 2004,37, 591–596. [CrossRef]
34.
Li, H.; Xiao, H.-G.; Yuan, J.; Ou, J. Microstructure of cement mortar with nano-particles. Compos. Part B Eng.
2004,35, 185–189. [CrossRef]
35.
Said, A.; Zeidan, M.S.; Bassuoni, M.; Tian, Y. Properties of concrete incorporating nano-silica. Constr. Build.
Mater. 2012,36, 838–844. [CrossRef]
36.
Szymanowski, J.; Sadowski, Ł. Functional and adhesive properties of cement-based overlays modified with
amorphous silica nanospheres. J. Adhes. 2019,96, 207–228. [CrossRef]
37.
Armentrout, J.B. The Investigation of Nano Silica in the Cement Hydration Process. Mater. Sci.
2009
, 267.
[CrossRef]
38.
Krivenko, P.; Sanytsky, M.; Kropyvnytska, T. The Effect of Nanosilica on the Early Strength of Alkali-Activated
Portland Composite Cements. Solid State Phenom. 2019,296, 21–26. [CrossRef]
39.
Marushchak, U.D.; Sanytsky, M.; Korolko, S.; Shabatura, Y.V.; Sydor, N. Development of nanomodifiedrapid
hardening fiber-reinforced concretes for special-purpose facilities. Eastern-European J. Enterp. Technol.
2018
,2,
34–41. [CrossRef]
40.
Sikora, P.; Cendrowski, K.; Elrahman, M.A.; Chung, S.-Y.; Wenelska, K.; Stephan, D. The effects of seawater on
the hydration, microstructure and strength development of Portland cement pastes incorporating colloidal
silica. Appl. Nanosci. 2020,10, 2627–2638. [CrossRef]
41.
Sikora, P.; Lootens, D.; Liard, M.; Stephan, D. The effects of seawater and nanosilica on the performance of
blended cements and composites. Appl. Nanosci. 2020,10, 5009–5026. [CrossRef]
42.
Shi, J.; Wang, J.; Muzenda, T.R.; Qu, Y.; Hou, P.; Cheng, X.; Liu, M. Effects of nanosilica on the hydration and
hardening properties of blended cement-based materials under heat curing. J. Therm. Anal. Calorim.
2020
,
141, 1317–1330. [CrossRef]
43.
Ma, C.; He, J.; Qin, T.; Long, G.; Du, Y.; Xie, Y. A comparison of the influence of micro- and nano-silica on
hydration kinetics of Portland cement under different temperatures. Constr. Build. Mater.
2020
,248, 118670.
[CrossRef]
44.
Li, H.; Ma, B.; Tan, H.; Li, H.; Liu, X.; Jiang, W.; Zhang, T.; Guo, Y. Influence of steam curing and nano silica
on hydration and microstructure characteristics of high volume fly ash cement system. Constr. Build. Mater.
2018,171, 83–95. [CrossRef]
45.
Sikora, P. The microstructural and thermal characteristics of silica nanoparticle-modified cement mortars after
exposure to high temperatures. Part I. Nanotechnol. Constr. A Sci. Internet-J. 2020,12, 108–115. [CrossRef]
46.
Elrahman, M.A.; Chung, S.-Y.; Sikora, P.; Rucinska, T.; Stephan, D. Influence of Nanosilica on Mechanical
Properties, Sorptivity, and Microstructure of Lightweight Concrete. Materials 2019,12, 3078. [CrossRef]
47.
PN-B-04500:1985 Zaprawy Budowlane—Badania Cech Fizycznych i Wytrzymało´sciowych; Polish Committee for
Standardization: Warsaw, Poland, 1985.
48.
Strzałkowski, J.; Garbali´nska, H. The Effect of Aggregate Shape on the Properties of Concretes with Silica
Fume. Materials 2020,13, 2780. [CrossRef]
49.
Yan, D.; Xie, L.; Qian, X.; Ruan, S.; Zeng, Q. Compositional Dependence of Pore Structure, Strengthand
Freezing-Thawing Resistance of Metakaolin-Based Geopolymers. Materials 2020,13, 2973. [CrossRef]
50.
El-Feky, M.S.; Youssef, P.; El-Tair, A.M.; Ibrahim, S.; Serag, M. Effect of nano silica addition on enhancing the
performance of cement composites reinforced with nano cellulose fibers. AIMS Mater. Sci.
2019
,6, 864–883.
[CrossRef]
51.
Skoczyla, K.N.; Rucinska, T. Strength and Durability of Cement Mortars Containing Nanosilica and Waste
Glass Fine Aggregate. Cem. Wapno Bet. 2018,3, 206–215.
52.
Zhang, Y.; Liu, H.; Tong, R.; Ren, J. Effect of Nano Silica on Freeze-Thaw Resistance of Cement-fl y Ash
Mortars, Cured in Corrosive Condition at Different Temperature. Cem. Wapno Bet. 2019,24, 137–153.
53.
Oltulu, M.; ¸Sahin, R. Pore structure analysis of hardened cement mortars containing silica fume and different
nano-powders. Constr. Build. Mater. 2014,53, 658–664. [CrossRef]
Materials 2020,13, 5800 15 of 15
54.
Quercia, G.G.; Spiesz, P.P.; Hüsken, G.G.; Brouwers, H.; Jos, J. SCC modification by use of amorphous
nano-silica. Cem. Concr. Compos. 2014,45, 69–81. [CrossRef]
55.
Zeidan, M.; Bassuoni, M.T.; Said, A. Physical salt attack on concrete incorporating nano-silica. J. Sustain.
Cem. Mater. 2016,6, 195–216. [CrossRef]
Publisher’s Note:
MDPI stays neutral with regard to jurisdictional claims in published maps and institutional
affiliations.
©
2020 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access
article distributed under the terms and conditions of the Creative Commons Attribution
(CC BY) license (http://creativecommons.org/licenses/by/4.0/).